Styrolution Terluran® SP-6 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Styrolution |
| Trade Name | Terluran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terluran® SP-6 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: High impact grade, suitable for extrusion.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Water Absorption | 1.03 % | 1.03 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.21 % | 0.21 % | 23°C/50% RH; ISO 62 |
| Melt Flow | 5.665 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.665 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 74.0 MPa @Load 36.5 kg, Time 30.0 sec |
10700 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 50mm/min; ISO 527-1/-2 |
| Elongation at Break | 9.0 % | 9.0 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 3.0 % | 3.0 % | 50mm/min; ISO 527-1/-2 |
| Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-1/-2 |
| Flexural Strength | 56.0 MPa | 8120 psi | ISO 178 |
| Izod Impact, Notched | 4.10 J/cm | 7.68 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 36.0 kJ/m² @Temperature 23.0 °C |
17.1 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 14.0 J/cm² @Temperature -30.0 °C |
66.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 - 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 - 61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ISO 75 |
| Vicat Softening Point | 90.0 °C | 194 °F | VST/B/50; ISO 306 |
| 103 °C | 217 °F | VST/A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.0054 @Frequency 100 Hz |
0.0054 @Frequency 100 Hz |
IEC 60250 |
| 0.0082 @Frequency 1.00e+6 Hz |
0.0082 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test Liquid A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Extrusion Pipes |
| 210 - 240 °C | 410 - 464 °F | Extrusion Sheets | |
| Drying Temperature | 80.0 °C | 176 °F | Pre-drying |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Europe | |
| Primary Processing Technique | Extrusion |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CQX10030 R3 Polypropylene, Mineral Reinforced, Scratch Resistant
- PolyOne Elastamax™ XL 0131-59 Styrene Butadiene Block Copolymer (SBC)
- DSM Akulon® K224-G3U (Dry) 15% Glass Reinforced Nylon 6 (North America) (discontinued **)
- Momentive Performance Materials Siloprenâ„¢ LSR 4050 Liquid Silicone Rubber - Healthcare
- Sylvin Technologies 8925-90 Natural PVC Extrusion Compound
- Solvay Specialty Polymers Halar® 6914 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Techmer ES HiFill® PA6/12 CF30 BK 30% Carbon Filled
- A. Schulman POLYBATCH™ Metallic Grey 80330/2
- Dow Corning 2-1912 FLUID
Copyright © lookpolymers.com All Rights Reserved