Category | Polymer , Thermoplastic , ABS Polymer |
Manufacturer | Styrolution |
Trade Name | Terluran® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Styrolution Terluran® HH-112 Q109 ABS.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
Melt Flow | 6.3 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.3 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Ball Indentation Hardness | 114 MPa @Load 36.5 kg, Time 30.0 sec |
16500 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
Tensile Strength, Yield | 58.0 MPa | 8410 psi | 50mm/min; ISO 527-1/-2 |
Elongation at Break | 8.0 % | 8.0 % | Nominal; ISO 527-1/-2 |
Elongation at Yield | 3.1 % | 3.1 % | 50mm/min; ISO 527-1/-2 |
Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 |
Flexural Strength | 81.0 MPa | 11700 psi | ISO 178 |
Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
14.0 J/cm² @Temperature 23.0 °C |
66.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 70.0 - 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 - 61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75 |
Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | ISO 75 |
Vicat Softening Point | 112 °C | 234 °F | VST/B/50; ISO 306 |
118 °C | 244 °F | VST/A/50; ISO 306 | |
Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
Dielectric Strength | 41.0 kV/mm | 1040 kV/in | K20/P50; IEC 60243-1 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 230 - 270 °C | 446 - 518 °F | Injection Molding |
Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | Injection Molding |
Drying Temperature | 80.0 °C | 176 °F | Pre-drying |
Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying |
Descriptive Properties | Value | Comments |
---|---|---|
Commercial Status | Europe | |
Primary Processing Technique | Injection Molding |