SABIC Innovative Plastics NORYL EXT115 PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL EXT115 PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS, Auto exterior grade, wax remover resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | SABIC - Japan Method |
| Elongation at Break | 120 % | 120 % | SABIC - Japan Method |
| Flexural Strength | 70.0 MPa | 10200 psi | ASTM D790 |
| Flexural Modulus | 2.05 GPa | 297 ksi | ASTM D790 |
| Izod Impact, Notched | 1.58 J/cm | 2.96 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 63.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C @Thickness 6.40 mm |
241 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EC486 DA Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polymax® Maxelast® P1980 TPE, PP Overmold or Standalone use
- Polykemi AB SCANAMID 66.6 C12^F30 Nylon 66/6, Glass Fiber, Reinforced
- H.C. Starck Amperit® 744 Aluminum Oxide-Titanium Oxide 87-13 (Al2O3 - TiO2)
- Saint-Gobain CHR® SG13-10(R) High Performance Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N550 (FEF) Filler
- Cossa Polimeri ESTAPROP H0260 MC/EC Conductive Polypropylene, Mineral Filled
- Alliance Polymers Viprene™ P70A-22U-BLK Thermoplastic Vulcanizate Elastomer
Copyright © lookpolymers.com All Rights Reserved