SABIC Innovative Plastics Valox® 507 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 507 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D 792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0020 in/in @Thickness 0.126 in |
SABIC Method |
| 0.0030 - 0.0060 cm/cm @Thickness 6.40 mm |
0.0030 - 0.0060 in/in @Thickness 0.252 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D 785 |
| Tensile Strength, Yield | 122 MPa | 17700 psi | SABIC - Japan Method |
| Elongation at Break | 3.0 % | 3.0 % | SABIC - Japan Method |
| Flexural Strength | 183 MPa | 26500 psi | ASTM D 790 |
| Flexural Modulus | 8.11 GPa | 1180 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.880 J/cm @Temperature 23.0 °C |
1.65 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C @Thickness 3.20 mm |
421 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Flammability, UL94 | HB @Thickness 0.830 mm |
HB @Thickness 0.0327 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D 257 |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten, PLC code 6; ASTM D 495 |
Users viewing this material also viewed the following:
- Ovation Polymers OpteSTAT™ NC PK 8010 Polyetheretherketone based Carbon Nanotube Compound
- Solvay Specialty Polymers Solef® 6008 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
- McDanel Advanced Ceramics SiAlON
- Stir SpA B 3015 AT S (PVC)
- Solvay RHODOPOL® TG Surfactant
- Covestro Makrolon® ET UV510 Polycarbonate
- EMS-Grivory Grivory® 2D 20 nat PA612
- E-Polymers Tekaloy® G70FR , Flame Retardant, Un-Reinforced PC/ABS Alloy
- BNZ Materials Blazecrete 3000 Dense Castable
- Arlon 51986XA015 0.016" (0.406 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved