Styrolution Terluran® EGP-7 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Styrolution |
| Trade Name | Terluran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terluran® EGP-7 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terluran EGP-7 is an extrusion grade with well balanced properties.UL 94 HBInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.21 % @Temperature 23.0 °C |
0.21 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.95 % @Temperature 23.0 °C |
0.95 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 97.0 MPa | 14100 psi | ISO 2039-1 |
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | ISO 527 |
| Elongation at Yield | 2.9 % | 2.9 % | ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 34.0 kJ/m² @Temperature 23.0 °C |
16.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 3.30 J/cm² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 - 110 µm/m-°C | 44.4 - 61.1 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ISO 75 |
| Vicat Softening Point | 100 °C @Load 5.10 kg |
212 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 107 °C @Load 1.02 kg |
225 °F @Load 2.25 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 203 - 250 °C | 397 - 482 °F | ISO 294 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Molding MR200 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Eastman Voridian D4053-A Polyethylene (discontinued **)
- Honeywell Aegis™ H135KQP Nylon 6 Extrusion Grade Homopolymer Film (discontinued **)
- Multibase Multi-Flex® D 3104 TPO Thermoplastic Polyolefin Elastomer
- UBE 1022MT2 Nylon 6 Monofilament (Drawing Ratio=4.5)
- Toyobo Vylopet® EMC130-01 Glass Reinforced Polyester, Standard Grade
- ExxonMobil Mobil 1 10W-40 Motorcycle Oil MX4T 4-Cycle
- ALM PA-616-GS Filled Nylon 12 Prototyping Polymer
- Fainplast Compounds GA 86/R Flexible PVC, Flame Retardant Sheathing
Copyright © lookpolymers.com All Rights Reserved