DuPont Performance Polymers Minlon® 73GM40 NC010 Nylon 6 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Minlon® 73GM40 NC010 Nylon 6
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Minlon® 73GM40 NC010 is a 40% mineral/glass reinforced, heat stabilized polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | DAM; ISO 1183 |
| Filler Content | 40 % | 40 % | DAM |
| Water Absorption | 1.6 % @Temperature 23.0 °C |
1.6 % @Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 5.6 % @Temperature 23.0 °C |
5.6 % @Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to | |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 2.00 mm |
0.0050 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm |
0.0070 in/in @Thickness 0.0787 in |
DAM; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa @Temperature 23.0 °C |
11600 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 140 MPa @Temperature 23.0 °C |
20300 psi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
DAM; ISO 527 |
| 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
50%RH; ISO 527 | |
| Tensile Modulus | 4.60 GPa @Temperature 23.0 °C |
667 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
| 8.30 GPa @Temperature 23.0 °C |
1200 ksi @Temperature 73.4 °F |
DAM; ISO 527 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1A |
| 5.50 kJ/m² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A | |
| 5.50 kJ/m² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1A | |
| 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU | |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA |
| 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 77.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
42.8 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ISO 11359-1/-2 |
| 77.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
42.8 µin/in-°F @Temperature 73.4 - 131 °F |
DAM; ASTM E 831 | |
| Melting Point | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | DAM; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | DAM |
| 270 °C | 518 °F | DAM; Optimum | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Features | Warp Resistant | DAM |
| Warpage, Low | DAM | |
| Filler | Glass/Mineral | DAM |
| Forms | Pellets | DAM |
| Generic | Nylon 6 | DAM |
| Heat Stabilized | Yes | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA6-(MD+GF)40< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA6 | DAM |
| Processing Method | Injection Molding | DAM |
| Product Category | Glass/Mineral Reinforced Resins | DAM |
| Low Warp Resins | DAM | |
| Region Available - Global | Yes | DAM |
| Resin Identification | PA6-(MD+GF)40 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
| Ultrasonic Weldable | Yes | DAM |
Users viewing this material also viewed the following:
- Murtfeldt Original Material ”S”® Black Antistatic Polyethylene, Conductive
- SABIC Innovative Plastics LNP STAT-KON RX05489 PA 66 (Asia Pacific)
- Techmer ES HiFill® HDPE GF15 15% Glass Filled
- Sumitomo Bakelite Durez® 23570 Phenolic, Compression Grade
- Cotronics Duralco™ 124 650°F (340°C) Silver Filled Epoxy
- Arkema Group Orgalloy® RS 6600 Nylon 66 Alloy, Rigid Grade (Conditioned)
- Arlon R36386C035 0.035" (0.889 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Daikin DAI-EL G-912 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content
Copyright © lookpolymers.com All Rights Reserved