- Styrolution Terblend® S NM-31 ASA / PA
Styrolution Terblend® S NM-31 ASA / PA
| Category | Polymer , Thermoplastic , ASA Polymer , Nylon |
| Manufacturer | Styrolution |
| Trade Name | Terblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terblend® S NM-31 ASA / PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terblend® S is a UV-stabilized ASA/PA blend with high impact strength, easy flow and pronounced color fastness. It is especially suitable for unpainted highly UV-exposed automotive interior parts.Enhanced UV resistance and color fastnessExcellent flow for high surface quality appearanceHigh impact strengthUV-stabilizedInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.5 % @Temperature 23.0 °C |
1.5 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
| Melt Flow | 60 g/10 min @Load 10.0 kg, Temperature 240 °C |
60 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Elongation at Yield | 3.3 % | 3.3 % | ISO 527 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 65.0 kJ/m² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 |
| Vicat Softening Point | 110 °C @Load 5.10 kg |
230 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 205 °C @Load 1.02 kg |
401 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | ISO 294 |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | ISO 294 |
Users viewing this material also viewed the following:
- Radici Radilon® A USZ200 (cond.) Nylon 66
- LG Chemical LUPOY RF3208F PC, Halogen Free Flame Retardance
- Lehmann & Voss ELECTRAFIL M-2386 Polycarbonate, with carbon fiber and PTFE
- SABIC Innovative Plastics LNP LUBRICOMP OCP36F PPS - Linear (Asia Pacific)
- Techmer ES Electrablend® PC C BK
- Techmer ES Luriblend® PA6/6 GF40 ML2 HS 40% Glass Filled
- SK Chemicals SKYTHANE® UB220 Ink Binder
- Master Bond MasterSil 709 One Part Silicone Meets MIL Spec
- ConocoPhillips ANDEROL® Assembly Lube Premium Quality White Mineral Oil Food Grade Grease, NLGI 1.5
Copyright © lookpolymers.com All Rights Reserved