- Styrolution Novodur® E211 ABS
Styrolution Novodur® E211 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Novodur® E211 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novodur E211 is a high heat extrusion grade and suitable for blow moldingInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ISO 294-4 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Elongation at Yield | 2.7 % | 2.7 % | ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 |
| Flexural Strength | 73.0 MPa | 10600 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 15.0 J/cm² @Temperature 23.0 °C |
71.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ISO 75 |
| Vicat Softening Point | 108 °C @Load 5.10 kg |
226 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.50 mm |
889 kV/in @Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- Orion Engineered Carbons CORAX® N 220 ASTM Carbon Black
- Ineos ABS Triax® 1180 ABS + Polyamide Blend (Conditioned) (discontinued **)
- Lehmann & Voss LUVOCOM® 21-7979 Polyamide 6/6T, with glass fiber, 8-mm-granulate
- LG Chemical LUCEL HI525L POM+Rubber, High Impact
- Sharadaa Ceramics ZAP 009 Smart Cast Application
- SMAC SMACTANE® SP Damping Material
- Techmer ES Electrablend® PA6/6 03003 CF Carbon Filled
- A. Schulman POLYFORT™ FXP 1245U UV Stable Copolymer Polypropylene
- Cotronics Resbond™ 919 High Temperature Ceramic Adhesive, High Resistance
- Techmer Lehvoss Compounds Luvotech™ J-4/35 NAT PA6/12 (discontinued **)
Copyright © lookpolymers.com All Rights Reserved