Styrolution Novodur® 4000PG ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Novodur® 4000PG ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novodur Ultra 4000PG is an injection molding grade especially suitable for electroplating, providing enhanced heat resistance.Information provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ISO 294-4 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 100 MPa | 14500 psi | ISO 2039-1 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ISO 527 |
| Elongation at Yield | 3.1 % | 3.1 % | ISO 527 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527 |
| Flexural Strength | 73.0 MPa | 10600 psi | ISO 178 |
| Flexural Modulus | 2.35 GPa | 341 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 23.0 kJ/m² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | ISO 75 |
| Vicat Softening Point | 107 °C @Load 5.10 kg |
225 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 38.0 kV/mm @Thickness 1.50 mm |
965 kV/in @Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Dissipation Factor | 0.0065 @Frequency 100 Hz |
0.0065 @Frequency 100 Hz |
IEC 60250 |
| 0.0085 @Frequency 1.00e+6 Hz |
0.0085 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 270 °C | 446 - 518 °F | ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® EX58F ABS (Asia Pacific)
- Lehmann & Voss LUVOCOM® 1301-7294/BL PPS, linear, with glass fiber
- Gromax BFG30-FU00B3 Nylon 6 30% Glass Filled (Conditioned)
- Schott WG225 Long Pass Filter
- Shin-Etsu Silicones LIMSâ„¢ KE2095-50AB Elastomer
- Formosa Plastics Formolene® 2520A Injection Molding Polypropylene
- Dow Nordel® IP 4725P Heat Resistant Molding
- Colorite Polymers 6507 General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved