DuPont Performance Polymers Delrin® 510GR NC000 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 510GR NC000 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® 510GR is a 10% glass reinforced acetal homopolymer for injection molding. It has high strength, stiffness, and high deflection temperature and excellent creep resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.47 g/cc
1.47 g/cc
ASTM D792
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
Filler Content 10 %
10 %
Water Absorption 0.16 %

@Temperature 23.0 °C
0.16 %

@Temperature 73.4 °F
Equilibrium 50%RH; ISO 62, Similar to
1.1 %

@Temperature 23.0 °C
1.1 %

@Temperature 73.4 °F
Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage 0.0090 - 0.011 cm/cm

@Thickness 3.20 mm
0.0090 - 0.011 in/in

@Thickness 0.126 in
Flow, 24h; ASTM D955
0.012 - 0.015 cm/cm

@Thickness 3.20 mm
0.012 - 0.015 in/in

@Thickness 0.126 in
Transverse, 24h; ASTM D955
Linear Mold Shrinkage, Flow 0.010 cm/cm

@Thickness 2.00 mm
0.010 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm

@Thickness 2.00 mm
0.014 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Flow 7.0 g/10 min

@Load 1.05 kg,
Temperature 190 °C
7.0 g/10 min

@Load 2.31 lb,
Temperature 374 °F
ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa

@Temperature 23.0 °C
13800 psi

@Temperature 73.4 °F
ISO 527
Tensile Strength 100 MPa

@Temperature 23.0 °C
14500 psi

@Temperature 73.4 °F
5mm/min (0.2in/min); ASTM D638
Tensile Stress 9.60 MPa

@Strain 0.54861 %,
Temperature 120 °C
1390 psi

@Strain 0.54861 %,
Temperature 248 °F
ISO 527
12.1 MPa

@Strain 0.48467 %,
Temperature 100 °C
1750 psi

@Strain 0.48467 %,
Temperature 212 °F
ISO 527
14.7 MPa

@Strain 0.48973 %,
Temperature 80.0 °C
2130 psi

@Strain 0.48973 %,
Temperature 176 °F
ISO 527
15.2 MPa

@Strain 0.46478 %,
Temperature 60.0 °C
2200 psi

@Strain 0.46478 %,
Temperature 140 °F
ISO 527
16.384 MPa

@Strain 1.0972 %,
Temperature 120 °C
2376.3 psi

@Strain 1.0972 %,
Temperature 248 °F
ISO 527
21.074 MPa

@Strain 0.96934 %,
Temperature 100 °C
3056.5 psi

@Strain 0.96934 %,
Temperature 212 °F
ISO 527
21.7 MPa

@Strain 0.42991 %,
Temperature 23.0 °C
3150 psi

@Strain 0.42991 %,
Temperature 73.4 °F
ISO 527
23.239 MPa

@Strain 1.6458 %,
Temperature 120 °C
3370.5 psi

@Strain 1.6458 %,
Temperature 248 °F
ISO 527
24.2 MPa

@Strain 0.43188 %,
Temperature 0.000 °C
3510 psi

@Strain 0.43188 %,
Temperature 32.0 °F
ISO 527
25.996 MPa

@Strain 0.92956 %,
Temperature 60.0 °C
3770.4 psi

@Strain 0.92956 %,
Temperature 140 °F
ISO 527
26.606 MPa

@Strain 0.97947 %,
Temperature 80.0 °C
3858.9 psi

@Strain 0.97947 %,
Temperature 176 °F
ISO 527
28.593 MPa

@Strain 1.454 %,
Temperature 100 °C
4147.1 psi

@Strain 1.454 %,
Temperature 212 °F
ISO 527
28.882 MPa

@Strain 2.1944 %,
Temperature 120 °C
4189.0 psi

@Strain 2.1944 %,
Temperature 248 °F
ISO 527
29.5 MPa

@Strain 0.47291 %,
Temperature -40.0 °C
4280 psi

@Strain 0.47291 %,
Temperature -40.0 °F
ISO 527
33.12 MPa

@Strain 2.743 %,
Temperature 120 °C
4804 psi

@Strain 2.743 %,
Temperature 248 °F
ISO 527
35.12 MPa

@Strain 1.9387 %,
Temperature 100 °C
5094 psi

@Strain 1.9387 %,
Temperature 212 °F
ISO 527
36.092 MPa

@Strain 3.2917 %,
Temperature 120 °C
5234.7 psi

@Strain 3.2917 %,
Temperature 248 °F
ISO 527
36.37 MPa

@Strain 1.4692 %,
Temperature 80.0 °C
5275 psi

@Strain 1.4692 %,
Temperature 176 °F
ISO 527
36.788 MPa

@Strain 1.3943 %,
Temperature 60.0 °C
5335.7 psi

@Strain 1.3943 %,
Temperature 140 °F
ISO 527
38.166 MPa

@Strain 3.8403 %,
Temperature 120 °C
5535.5 psi

@Strain 3.8403 %,
Temperature 248 °F
ISO 527
38.773 MPa

@Strain 0.85983 %,
Temperature 23.0 °C
5623.6 psi

@Strain 0.85983 %,
Temperature 73.4 °F
ISO 527
39.505 MPa

@Strain 4.3889 %,
Temperature 120 °C
5729.7 psi

@Strain 4.3889 %,
Temperature 248 °F
ISO 527
40.236 MPa

@Strain 4.9375 %,
Temperature 120 °C
5835.7 psi

@Strain 4.9375 %,
Temperature 248 °F
ISO 527
40.458 MPa

@Strain 2.4233 %,
Temperature 100 °C
5867.9 psi

@Strain 2.4233 %,
Temperature 212 °F
ISO 527
40.763 MPa

@Strain 5.4861 %,
Temperature 120 °C
5912.2 psi

@Strain 5.4861 %,
Temperature 248 °F
ISO 527
42.383 MPa

@Strain 0.86376 %,
Temperature 0.000 °C
6147.1 psi

@Strain 0.86376 %,
Temperature 32.0 °F
ISO 527
44.193 MPa

@Strain 1.9589 %,
Temperature 80.0 °C
6409.7 psi

@Strain 1.9589 %,
Temperature 176 °F
ISO 527
44.729 MPa

@Strain 2.908 %,
Temperature 100 °C
6487.4 psi

@Strain 2.908 %,
Temperature 212 °F
ISO 527
46.286 MPa

@Strain 1.8591 %,
Temperature 60.0 °C
6713.2 psi

@Strain 1.8591 %,
Temperature 140 °F
ISO 527
47.928 MPa

@Strain 3.3927 %,
Temperature 100 °C
6951.4 psi

@Strain 3.3927 %,
Temperature 212 °F
ISO 527
50.101 MPa

@Strain 3.8774 %,
Temperature 100 °C
7266.5 psi

@Strain 3.8774 %,
Temperature 212 °F
ISO 527
50.504 MPa

@Strain 2.4487 %,
Temperature 80.0 °C
7325.0 psi

@Strain 2.4487 %,
Temperature 176 °F
ISO 527
51.257 MPa

@Strain 0.94582 %,
Temperature -40.0 °C
7434.2 psi

@Strain 0.94582 %,
Temperature -40.0 °F
ISO 527
51.292 MPa

@Strain 4.362 %,
Temperature 100 °C
7439.3 psi

@Strain 4.362 %,
Temperature 212 °F
ISO 527
51.962 MPa

@Strain 4.8467 %,
Temperature 100 °C
7536.5 psi

@Strain 4.8467 %,
Temperature 212 °F
ISO 527
53.401 MPa

@Strain 1.2897 %,
Temperature 23.0 °C
7745.2 psi

@Strain 1.2897 %,
Temperature 73.4 °F
ISO 527
54.099 MPa

@Strain 2.3239 %,
Temperature 60.0 °C
7846.4 psi

@Strain 2.3239 %,
Temperature 140 °F
ISO 527
55.126 MPa

@Strain 2.9384 %,
Temperature 80.0 °C
7995.4 psi

@Strain 2.9384 %,
Temperature 176 °F
ISO 527
58.223 MPa

@Strain 3.4281 %,
Temperature 80.0 °C
8444.5 psi

@Strain 3.4281 %,
Temperature 176 °F
ISO 527
58.653 MPa

@Strain 1.2956 %,
Temperature 0.000 °C
8506.9 psi

@Strain 1.2956 %,
Temperature 32.0 °F
ISO 527
60.039 MPa

@Strain 3.9179 %,
Temperature 80.0 °C
8707.9 psi

@Strain 3.9179 %,
Temperature 176 °F
ISO 527
60.581 MPa

@Strain 2.7887 %,
Temperature 60.0 °C
8786.5 psi

@Strain 2.7887 %,
Temperature 140 °F
ISO 527
60.788 MPa

@Strain 4.4076 %,
Temperature 80.0 °C
8816.6 psi

@Strain 4.4076 %,
Temperature 176 °F
ISO 527
61.056 MPa

@Strain 4.8973 %,
Temperature 80.0 °C
8855.4 psi

@Strain 4.8973 %,
Temperature 176 °F
ISO 527
64.901 MPa

@Strain 1.7197 %,
Temperature 23.0 °C
9413.1 psi

@Strain 1.7197 %,
Temperature 73.4 °F
ISO 527
65.806 MPa

@Strain 3.2535 %,
Temperature 60.0 °C
9544.4 psi

@Strain 3.2535 %,
Temperature 140 °F
ISO 527
69.369 MPa

@Strain 3.7182 %,
Temperature 60.0 °C
10061 psi

@Strain 3.7182 %,
Temperature 140 °F
ISO 527
71.407 MPa

@Strain 1.7275 %,
Temperature 0.000 °C
10357 psi

@Strain 1.7275 %,
Temperature 32.0 °F
ISO 527
71.424 MPa

@Strain 4.183 %,
Temperature 60.0 °C
10359 psi

@Strain 4.183 %,
Temperature 140 °F
ISO 527
71.529 MPa

@Strain 1.4187 %,
Temperature -40.0 °C
10374 psi

@Strain 1.4187 %,
Temperature -40.0 °F
ISO 527
72.353 MPa

@Strain 4.6478 %,
Temperature 60.0 °C
10494 psi

@Strain 4.6478 %,
Temperature 140 °F
ISO 527