Wolf Kunststoff ZEDEX® ZX-100K A1K Polymer Alloy

Category Polymer , Thermoplastic
Manufacturer Wolf Kunststoff
Trade Name ZEDEX®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Wolf Kunststoff ZEDEX® ZX-100K A1K Polymer Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Main Characteristics: Hard; Stiff; Tough; High fatigue strength; Good weather resistance; Good machinability; FDA compliant LABS; PTFE and silicone-free; KTW approved; Stress resistantApplications: Handling, Vessel and Pump, Steel and Water, Chemical Engineering, Automitve Technology, Machine ToolsInformation provided by Zedex
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
Water Absorption 0.30 %

@Temperature 23.0 °C
0.30 %

@Temperature 73.4 °F
RMC 93%; DIN EN ISO 62
Moisture Absorption at Equilibrium 0.50 %
0.50 %
DIN EN ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore A >= 100
>= 100
DIN 53505
Hardness, Shore D 84
84
DIN 53505
Ball Indentation Hardness 136 MPa
19700 psi
DIN 2039
Tensile Strength at Break 70.0 MPa
10200 psi
DIN EN ISO 527
Tensile Strength 78.0 MPa
11300 psi
DIN EN ISO 527
Tensile Stress 22.0 MPa

@Strain 1.00 %,
Time 3.60e+6 sec
3190 psi

@Strain 1.00 %,
Time 1000 hour
DIN 53444
Tensile Strength, Yield 65.0 MPa
9430 psi
Elastic Limit
78.0 MPa
11300 psi
DIN EN ISO 527
Elongation at Break 9.5 %
9.5 %
9.5 %
9.5 %
DIN EN ISO 527
Elongation at Yield 1.6 %
1.6 %
Elastic Yield Point
4.0 %
4.0 %
DIN EN ISO 527
6.0 %
6.0 %
Elongation at Maximum Force; DIN EN ISO 527
6.1 %
6.1 %
Flexural; DIN EN ISO 178
Tensile Modulus 2.90 GPa
421 ksi
DIN EN ISO 527
Flexural Strength 96.0 MPa
13900 psi
Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
117 MPa
17000 psi
DIN EN ISO 178
Flexural Modulus 3.30 GPa
479 ksi
DIN EN ISO 178
Compressive Strength 75.0 MPa
10900 psi
Elastic Limit
30.0 MPa

@Time 3.60e+7 sec
4350 psi

@Time 10000 hour
60.0 MPa

@Time 360000 sec
8700 psi

@Time 100 hour
75.0 MPa

@Time 36.0 sec
10900 psi

@Time 0.0100 hour
30.0 MPa

@Strain 3.50 %
4350 psi

@Strain 3.50 %
DIN EN ISO 604
Compressive Modulus 3.15 GPa
457 ksi
DIN EN ISO 604
Fatigue Strength 52.0 MPa

@# of Cycles 1.00e+6
7540 psi

@# of Cycles 1.00e+6
1 Hz
K Factor (ISO) 0.70 µm/km

@Temperature 20.0 °C
0.70 µm/km

@Temperature 68.0 °F
2.1 µm/km

@Temperature 100 °C
2.1 µm/km

@Temperature 212 °F
Charpy Impact Unnotched 5.40 J/cm²
25.7 ft-lb/in²
EN ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
EN ISO 179/1eA
Coefficient of Friction, Dynamic 0.080

@Temperature 20.0 °C
0.080

@Temperature 68.0 °F
Dry Operation
0.15

@Temperature 100 °C
0.15

@Temperature 212 °F
Dry Operation
Coefficient of Friction, Static 0.11

@Temperature 20.0 °C
0.11

@Temperature 68.0 °F
Dry Operation
Tensile Creep Modulus, 1000 hours 2000 MPa
290000 psi
At 1% Deformation; DIN 53444
Limiting Pressure Velocity 0.133 MPa-m/sec
3800 psi-ft/min
v = 100m/min
0.133 MPa-m/sec
3800 psi-ft/min
v = 200m/min
0.432 MPa-m/sec
12300 psi-ft/min
v = 10m/min
0.583 MPa-m/sec
16600 psi-ft/min
v = 1m/min
Compression Set 6.0 %
6.0 %
Elastic Compression Limit
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C

@Temperature <=100 °C
44.4 µin/in-°F

@Temperature <=212 °F
ISO E 830
120 µm/m-°C

@Temperature <=150 °C
66.7 µin/in-°F

@Temperature <=302 °F
ISO E 831
Specific Heat Capacity 1.06 J/g-°C
0.253 BTU/lb-°F
DSC
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 250 °C
482 °F
DSC
Maximum Service Temperature, Air 65.0 °C
149 °F
Pressed Bushings
110 °C
230 °F
Continuous
140 °C
284 °F
Short Term (3h)
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
DIN EN ISO 75
Glass Transition Temp, Tg 78.0 °C
172 °F
DSC
Flammability, UL94 HB
HB
Oxygen Index 24 %
24 %
DIN EN ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+14 ohm-cm
2.00e+14 ohm-cm
IEC 93
Surface Resistance 6.00e+10 ohm
6.00e+10 ohm
IEC 93
Dielectric Constant 3.4

@Frequency 110 Hz
3.4

@Frequency 110 Hz
IEC 250
Dielectric Strength 21.5 kV/mm
546 kV/in
IEC 243
Dissipation Factor 0.015
0.015
IEC 112
0.077

@Frequency 1.00 Hz
0.077

@Frequency 1.00 Hz
Comparative Tracking Index 305 V
305 V
IEC 112
Descriptive Properties Value Comments
Alignment Adjustment 5
Nominal Scale: 1, low; 10, high
Chemical Sterilization 7
Nominal Scale: 1, low; 10, high
Color White
Creep Resistance 3
Nominal Scale: 1, low; 10, high
Dimensional Stability with Thermal Expansion 3
Nominal Scale: 1, low; 10, high
FDA Compliant Applicable
Free from PTFE Applicable
Free from Silicon Applicable
Gamma-rays Radiation Sterilization 3
Nominal Scale: 1, low; 10, high
High Precision Bushings (negative clearance) Applicable
Injection Molded Parts Limited
Machined Parts Applicable
Moist Heat Sterilization 6
Nominal Scale: 1, low; 10, high
Plastic Granules Limited
Rate of Desorption 1.83E-06
a = .44
Resistance Against dust, Dirt, Abrasive Substances 6
Nominal Scale: 1, low; 10, high
Resistance Against Hot Water 80
Resistance to Chemicals 7
Nominal Scale: 1, low; 10, high
Resistant Against Disinfectant Applicable
Rods up to Øe (de) Applicable
ROHS/WEEE Applicable
Sheets up to Maximum Thickness Applicable
Sliding Velocity 100
Suitable for Outdoor Use 8
Nominal Scale: 1, low; 10, high
Suitable for Use in Water Applicable
Suitable for Vacuum Applicable
Tubes (hollow rods) up to Øe (de) Applicable
UV Rays Resistance 9
Nominal Scale: 1, low; 10, high
UV-Sterilization 7
Nominal Scale: 1, low; 10, high