Styrolution NAS® 30 Series High Performance Styrenic
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | Styrolution |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution NAS® 30 Series High Performance Styrenic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
It has sparkling clarity and good scratch resistance. This easily processed copolymer blends well with K-Resin® to modify flexibility, surface hardness, and HDT. It meets USP XXIII Spec. of Class VI Plastics for all grades except UV-stabilized grades.Information provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 2.2 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.2 g/10 min @Load 11.0 lb, Temperature 392 °F |
Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 75 | 75 | ASTM D785 |
| Tensile Strength, Ultimate | 60.7 MPa | 8800 psi | 0.2 in/min;ASTM D638 |
| Elongation at Break | 2.3 % | 2.3 % | ASTM D638 |
| Modulus of Elasticity | 3.24 GPa | 470 ksi | ASTM D638 |
| Flexural Yield Strength | 101 MPa | 14600 psi | 0.05 in/min; ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | .05 in/min;ASTM D790 |
| Izod Impact, Notched | 0.200 J/cm | 0.375 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | Annealed, 1.8 Mpa;ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.56 | 1.56 | ASTM D542 |
| Haze | 0.27 % | 0.27 % | ASTM D1003 |
| Transmission, Visible | 91.4 % | 91.4 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 216 °C | 360 - 421 °F | |
| Middle Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Front Barrel Temperature | 210 - 243 °C | 410 - 469 °F | |
| Melt Temperature | 210 - 243 °C | 410 - 469 °F | |
| Mold Temperature | 32.0 - 60.0 °C | 89.6 - 140 °F | |
| Drying Temperature | 82.0 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPS7 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific)
- Abatron AboWeld 8012-4/AboCure 8012-4 Epoxy (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-7916-1 PEEK, with carbon fiber
- Silberline Sparkle Silvex® Premier 838-20-C
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.5 PHR Sulfur
- DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 150 Gauge
- Fainplast Compounds HGK 83 Flexible PVC, Sheathing for High Temperatures Lead Free
- Dow Nordel® IP 4570 General Purpose Compound
Copyright © lookpolymers.com All Rights Reserved