Styrolution Luran® 368 R SAN

Category Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded
Manufacturer Styrolution
Trade Name Luran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Luran® 368 R SAN.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General-purpose grade with well-balanced properties intended for both injection molding and extrusion.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Melt Flow 10 g/10 min

@Load 10.0 kg,
Temperature 220 °C
10 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 104 MPa

@Temperature -40.0 °C
15100 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 75.0 MPa
10900 psi
5mm/min; ISO 527
Tensile Strength, Yield 75.0 MPa
10900 psi
2 in/min; ASTM Test
32.0 MPa

@Temperature 80.0 °C
4640 psi

@Temperature 176 °F
ISO Data
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
3.0 %
3.0 %
2 in/min; ASTM Test
3.7 %

@Temperature -40.0 °C
3.7 %

@Temperature -40.0 °F
ISO Data
Elongation at Yield 2.1 %

@Temperature 80.0 °C
2.1 %

@Temperature 176 °F
ISO Data
Tensile Modulus 3.70 GPa
537 ksi
1mm/min; ISO 527
3.80 GPa
551 ksi
ASTM Test
Flexural Strength 125 MPa
18100 psi
ASTM Test
Charpy Impact Unnotched 1.80 J/cm²
8.57 ft-lb/in²
ISO 179
1.80 J/cm²

@Temperature -30.0 °C
8.57 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
ISO 179
Tensile Creep Modulus, 1 hour 3500 MPa
508000 psi
ISO 899
Tensile Creep Modulus, 1000 hours 2800 MPa
406000 psi
ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359
Deflection Temperature at 0.46 MPa (66 psi) 102 °C
216 °F
annealed; ASTM Test
102 °C
216 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
annealed; ASTM Test
98.0 °C
208 °F
ISO 75
Vicat Softening Point 106 °C
223 °F
Rate "A" Loading 1 (50 degC/h 10N); ASTM Test
106 °C
223 °F
(50 °C/h / 50N) - B/50; ISO 306
Oxygen Index 18 %
18 %
ISO 4589-1/-2
Optical Properties Metric English Comments
Transmission, Visible 80 %
80 %
unknown thickness
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+13 ohm
>= 1.00e+13 ohm
IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 60243-1
Dissipation Factor 0.0040

@Frequency 100 Hz
0.0040

@Frequency 100 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 425 V
425 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Injection molding
Mold Temperature 60.0 °C
140 °F
Injection molding
98.0 °C
208 °F
Ejection temperature
Injection Velocity 200 mm/sec
7.87 in/sec
Injection molding
Descriptive Properties Value Comments
Color Clear
Commercial Status North America and Europe
FDA Yes
Form Pellets
Impact Modified No
NSF Std. 51 No
NSF Std. 61 No
Primary Processing Technique Extrusion
Processing Injection Molding
Other Extrusion
Profile Extrusion
Sheet Extrusion
Thermoforming
UL.UL-C Yes