SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Conductive GTX, CTE 7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.900 % | 0.900 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 3.0 % | 3.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
8.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 15 % | 15 % | Type I, 50 mm/min; ASTM D638 |
| 20 % | 20 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 |
| 3.25 GPa | 471 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.70 GPa | 392 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.80 GPa | 406 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C |
1.31 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature -40.0 - 60.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -40.0 - 60.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| 75.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
41.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 185 °C @Thickness 3.20 mm |
365 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 192 °C | 378 °F | Rate B/50; ASTM D1525 |
| 198 °C | 388 °F | Rate B/50; ISO 306 | |
| 200 °C | 392 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- RheTech Products P254-01 Polypropylene Copolymer, Black
- Solvay TECHNYLSTARâ„¢ S 218 V30 PA6, 30% glass filled, Conditioned
- Polyplastics Duranex® 7307 Polybutylene Terephthalate (PBT), Super low warpage, GF filled
- A. Schulman POLYBATCH™ Blue 4500GZ Concentrate Based in Low-Density Polyethylene
- TSE Industries Millathane® 28 Millable Polyester Polyurethane Rubber
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- Eagle Brass 210 Gilding Metal, Extra Spring
- DuPont Performance Polymers Delrin® SC699 NC010 Acetal (POM) (Unverified Data**)
- 3M FM071 Indoor UL Recognized Clear Polyester Overlaminate Label Product
Copyright © lookpolymers.com All Rights Reserved