Star Plastics PC/ABSQX7005 Molding Grade PC/ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Star Plastics, Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Star Plastics PC/ABSQX7005 Molding Grade PC/ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Star Plastics, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
ASTM D955
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 15 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 48.3 MPa
7000 psi
ASTM D638
Tensile Modulus 2.14 GPa
310 ksi
ASTM D638
Flexural Yield Strength 68.9 MPa
10000 psi
ASTM D790
Flexural Modulus 2.14 GPa
310 ksi
ASTM D790
Izod Impact, Notched 5.34 J/cm
10.0 ft-lb/in
73°F, 0.125 in.; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
unannealed, .125in; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 238 - 274 °C
460 - 525 °F
Middle Barrel Temperature 260 - 274 °C
500 - 525 °F
Front Barrel Temperature 260 - 288 °C
500 - 550 °F
Nozzle Temperature 260 - 288 °C
500 - 550 °F
Melt Temperature 260 - 288 °C
500 - 550 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 87.8 - 110 °C
190 - 230 °F
Dry Time 3 - 4 hour
3 - 4 hour
Back Pressure 0.172 - 0.689 MPa
25.0 - 100 psi
Screw Speed 25 - 75 rpm
25 - 75 rpm