- Solvay Technyl® C50H2 Nylon 6, Flame Retardant, Heat Stabilized
Solvay Technyl® C50H2 Nylon 6, Flame Retardant, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® C50H2 Nylon 6, Flame Retardant, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183-A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
| Tensile Modulus | 3.70 GPa | 537 ksi | ISO 527 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-2 |
| Flammability, UL94 | V-0 @Thickness >=0.380 mm |
V-0 @Thickness >=0.0150 in |
NC, BK, Gy colors |
| V-0 @Thickness >=0.750 mm |
V-0 @Thickness >=0.0295 in |
All colors | |
| V-0 @Thickness >=1.50 mm |
V-0 @Thickness >=0.0591 in |
All colors | |
| V-0 @Thickness >=3.00 mm |
V-0 @Thickness >=0.118 in |
All colors |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | |
| Hot Wire Ignition, HWI | 7.0 - 15 sec @Thickness >=0.380 mm |
7.0 - 15 sec @Thickness >=0.0150 in |
NC, BK, Gy colors |
| 7.0 - 15 sec @Thickness >=0.750 mm |
7.0 - 15 sec @Thickness >=0.0295 in |
All colors | |
| 15 - 30 sec @Thickness >=1.50 mm |
15 - 30 sec @Thickness >=0.0591 in |
All colors | |
| 30 - 60 sec @Thickness >=3.00 mm |
30 - 60 sec @Thickness >=0.118 in |
All colors | |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 0.380 mm |
>= 120 arcs @Thickness 0.0150 in |
NC, BK, Gy colors |
| >= 120 arcs @Thickness 0.750 mm |
>= 120 arcs @Thickness 0.0295 in |
All colors | |
| >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
All colors | |
| >= 120 arcs @Thickness 3.00 mm |
>= 120 arcs @Thickness 0.118 in |
All colors | |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 254 mm/min | 0.000 - 10.0 in/min |
Users viewing this material also viewed the following:
- Victrex® PEEK 150XF Polyetheretherketone, Unreinforced
- Imerys Kingsley - Rogersâ„¢ Kaolin
- LG Chemical GPPS 20HR(E) PS, High Transparency, Heat Resistance
- Mitsui MILEXâ„¢ XL-225MB Phenol Aralkyl Resin, Standard Grade
- Solvay TECHNYL® C 502XT PA6, DRY
- Shin-Etsu Silicones KSG-210 Fluid
- A. Schulman CP80-01 Linear Low-Density Polyethylene
- Goodfellow Cobalt/Silicon/Boron/Manganese Alloy
- DuPont Bynel® 3930 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin
- Bhansali Engineering Abstron KU650NH ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved