- Lehmann & Voss LUVOCOM® 3/CF/30 Polyamide 6, with carbon fiber
Lehmann & Voss LUVOCOM® 3/CF/30 Polyamide 6, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 3/CF/30 Polyamide 6, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressElectrically conductive, suitable for continuous discharging of statically generated electricity.Handles, levers, rollers, extrusion profiles.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 210 MPa | 30500 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| 3.0 % | 3.0 % | flexural | |
| Modulus of Elasticity | 16.0 GPa | 2320 ksi | |
| Flexural Strength | 315 MPa | 45700 psi | |
| Flexural Modulus | 15.0 GPa | 2180 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | flatwise; ISO 179 1fU |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.500 W/m-K | 3.47 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| 210 °C | 410 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | |
| Insulation Resistance | <= 1000 ohm | <= 1000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | mass temp |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | |
| Zone 1 | 250 - 270 °C | 482 - 518 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 75.0 °C @Time 36000 - 57600 sec |
167 °F @Time 10.0 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Omnia Plastica PP Polypropylene
- Pau Tai UNISTAB RP-33K Solid Complex Stabilizer
- PolyOne Geon™ Vinyl Flexible A48248D Polyvinyl Chloride, Flexible (PVC, Flexible)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N330 (HAF) Filler
- Techmer ES HiFill FR® PA6/6 GF40 FR HS L 40% Glass Filled
- DSM Arnitel® PL650 Polyether Ester Elastomer (European and Asian Grade)
- ACC QM 264 QSI Quantum Silicones 60 Durometer Addition Cure Moldmaking Material
- Adamas Adalon® 503 PTFE, 0.1% MoS2
- Ascend Performance Materials Vydyne® 47H BK0644 Nylon 66, Impact Modified, DAM
Copyright © lookpolymers.com All Rights Reserved