SABIC Innovative Plastics Lexan® IP300 PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Lexan®
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	SABIC Innovative Plastics Lexan® IP300 PC.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Improved toughness/impact strength at ambient/low temperatures for automotive instrument panels, knee bolsters and trim. Range gray and black only.This data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.18 g/cc	1.18 g/cc	ASTM D 792
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm <br>@Thickness 3.20 mm	0.0050 - 0.0070 in/in <br>@Thickness 0.126 in	SABIC Method
Melt Flow	18 g/10 min <br>@Load 1.20 kg,<br> Temperature 300 °C	18 g/10 min <br>@Load 2.65 lb,<br> Temperature 572 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	65	65	ASTM D 785
Tensile Strength at Break	55.0 MPa	7980 psi	Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield	57.0 MPa	8270 psi	Type I, 50 mm/min; ASTM D 638
Elongation at Break	75 %	75 %	Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength	84.0 MPa	12200 psi	1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus	2.13 GPa	309 ksi	1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched	5.01 J/cm <br>@Temperature -30.0 °C	9.39 ft-lb/in <br>@Temperature -22.0 °F	ASTM D 256
	5.87 J/cm <br>@Temperature 23.0 °C	11.0 ft-lb/in <br>@Temperature 73.4 °F	ASTM D 256
Impact Test	50.0 J <br>@Temperature 23.0 °C	36.9 ft-lb <br>@Temperature 73.4 °F	Instrumented Impact Energy @ peak; ASTM D 3763
	50.0 J <br>@Temperature -30.0 °C	36.9 ft-lb <br>@Temperature -22.0 °F	Instrumented Impact Energy @ peak; ASTM D 3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	121 °C <br>@Thickness 3.20 mm	250 °F <br>@Thickness 0.126 in	unannealed; ASTM D 648