Solvay Technyl® A 216 V40 40% Glass Filled Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 216 V40 40% Glass Filled Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | 24 Hr.; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 225 MPa | 32600 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ASTM D638 |
| Flexural Strength | 305 MPa | 44200 psi | ASTM D790 |
| Flexural Modulus | 10.7 GPa | 1550 ksi | ASTM D790 |
| Izod Impact, Notched | 1.35 J/cm | 2.53 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263.0 °C | 505.4 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Compression Zone |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Nozzle Temperature | 271 - 279 °C | 520 - 535 °F | |
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Surface |
| Drying Temperature | 80.0 °C | 176 °F | Dehumidifying Dryer |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Fill Speed | 200 - 300 mm/sec | 7.87 - 11.8 in/sec | Peripheral Screw Speed |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed (cm3/sec) | 120 - 170 cm3/sec |
Users viewing this material also viewed the following:
- MV Labs AL530 AlF3.3H2O Aluminum fluoride trihydrate
- Polymer Resources PC-GP4-[color]-5 Polycarbonate, FDA-compliant Feedstocks, Easy Flow
- Plastcom SLOVAMID 6 HI/1 TLS PA6, improved strength
- FloMet Fe-3% Si Soft Magnetic Alloy
- Samsung Cheil Industries Starex® SG-101 Expandable Polystyrene (EPS) High Expansion
- Eurostar Staramide PF005 PA6, 25% Glass Fiber Filled, Injection Molded
- BASF Lupranate® 5030 Isocyanate
- 3M Scotch-Weld™ DP190 Gray Epoxy Adhesive
- A. Schulman ComAlloy Lubrilon® 620 Nylon 6/6, Glass Fiber/Molybdenum Disulfide Filled, Flow Enhanced
- DuPont Performance Polymers Zytel® HTN 52G35HSL BK083 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved