Braskem TS7003 LDPE Blown Film Extrusion Polyethylene

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Braskem
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem TS7003 LDPE Blown Film Extrusion Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TS7003 is a low-density polyethylene (LDPE) with high molecular weight that offers high mechanical strength and toughness even at low temperatures. Additionally, this product is easily processed. The product was developed to meet the requirements for automatic packaging. The additive package provides a low coefficient of friction (COF) allowing high productivity on the packaging lines. This product is identified as PE 115 according to ASTM D-4976-04a standard specification. It has antiblocking and slip agent additives. Its applications include: films for automatic packaging of liquids (milk, yot, juices, etc.), packaging for frozen food (meat, chicken, seafood, fries, etc.), and blow molding flexible packaging.

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ASTM-D792
Melt Flow	0.27 g/10 min @Load 2.16 kg, Temperature 190 °C	0.27 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	370 %	370 %	ASTM-D882
Film Elongation at Break, TD	680 %	680 %	ASTM-D882
Secant Modulus, MD	0.140 GPa	20.3 ksi	2% Secant Modulus; ASTM-D882
Secant Modulus, TD	0.150 GPa	21.8 ksi	2% Secant Modulus; ASTM-D882
Elmendorf Tear Strength MD	300 g	300 g	ASTM-D1922
Elmendorf Tear Strength TD	220 g	220 g	ASTM-D1922
Elmendorf Tear Strength, MD	6.00 g/micron	152 g/mil	ASTM-D1922
Elmendorf Tear Strength, TD	4.40 g/micron	112 g/mil	ASTM-D1922
Dart Drop	3.80 g/micron	96.5 g/mil	ASTM-D1709
Dart Drop Test	190 g	0.419 lb	ASTM-D1709
Film Tensile Strength at Break, MD	27.0 MPa	3920 psi	ASTM-D882
Film Tensile Strength at Break, TD	24.0 MPa	3480 psi	ASTM-D882

Optical Properties	Metric	English	Comments
Haze	13 %	13 %	ASTM-D1003
Gloss	70 %	70 %	Angle 60°; ASTM-D2457

Processing Properties	Metric	English	Comments
Die Opening	0.100 cm	0.0394 in	Blow Film Extrusion
Blow-up Ratio (BUR)	2.0 - 3.0	2.0 - 3.0	Blow Film Extrusion

Descriptive Properties	Value	Comments
Mass Temperature (°C)	180-205	Blow Film Extrusion
Temperature Profile (°C)	160-205	Blow Film Extrusion

Users viewing this material also viewed the following: