Solvay TECHNYL® C 52G1 V20 PA6, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® C 52G1 V20 PA6, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Halogen and Red Phosphorous free fire resistant polyamide PA6 Glass reinforced for injection molding of thin walled partsAvailable in: Asia Pacific, Europe, Latin America and North America Product Applications: This grade is Halogen and Red Phosphorous free fire resistant flame retardant grade is particularly suitable for equipment requiring robust glow-wire resistance with excellent molding and electrical performance, such as for MCB housings, contactors and switches and sockets. This grade is available in Grey, White, Natural and Black colors. Laser marking grades and other colors are available upon request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183/A
Water Absorption 1.1 %

@Temperature 23.0 °C,
Time 86400 sec
 1.1 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 92.0 MPa
13300 psi
ISO 527 Type 1A
Elongation at Break 2.9 %
2.9 %
ISO 527 Type 1A
Tensile Modulus 6.70 GPa
972 ksi
ISO 527 Type 1A
Charpy Impact Unnotched 3.90 J/cm²
18.6 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.310 J/cm²

@Temperature -30.0 °C
 1.48 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.320 J/cm²

@Temperature 23.0 °C
 1.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
ISO 75/Af
Flammability, UL94 V-2

@Thickness 0.800 mm
 V-2

@Thickness 0.0315 in
 1210
V-2

@Thickness 1.60 mm
 V-2

@Thickness 0.0630 in
 1210
V-2

@Thickness 3.20 mm
 V-2

@Thickness 0.126 in
 1210
Oxygen Index 29 %
29 %
ISO 4589
Glow Wire Test 700 °C

@Thickness 1.60 mm
 1290 °F

@Thickness 0.0630 in
 ignition temperature; ISO 60695-2-13
725 °C

@Thickness 0.800 mm
 1340 °F

@Thickness 0.0315 in
 ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 ISO 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 ISO 60695-2-12
960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Dielectric Strength 31.0 kV/mm
787 kV/in
IEC 60243
Comparative Tracking Index 450 V
450 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 220 - 230 °C
428 - 446 °F
Front Barrel Temperature 245 - 255 °C
473 - 491 °F
Mold Temperature 80.0 °C
176 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 230-240°C