Total PPH 3276 Polypropylene, Oriented Film Extrusion Grade
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Total Atofina |
| Trade Name | PPH |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total PPH 3276 Polypropylene, Oriented Film Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Homopolymer film gradeLow Residuals – Fina 3276 utilizes the new Fina proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock – Fina 3276 is available with custom slip and antiblock packages.FDA – Fina 3276 complies with all application FDA regulations for food contact applications.Recommended Applications - Fina 3276 is recommended in orientation processes for manufacture of packaging tapes and films.Processing – Fina 3276 resin processes on oriented film extrusion equipment with typical melt temperatures of 450- 525°F (232-274°C)Data provided by the manufacturer, Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 4.70 g/m²/day @Temperature 37.8 °C |
0.303 g/100 in²/day @Temperature 100 °F |
90% RH; thickness not specified; ASTM E96 |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 152 MPa | 22000 psi | |
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882 |
| Film Elongation at Break, TD | 50 % | 50 % | ASTM D882 |
| Secant Modulus, MD | 2.41 GPa | 350 ksi | ASTM D882 |
| Secant Modulus, TD | 4.14 GPa | 600 ksi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | DSC |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 274 °C | 450 - 525 °F | oriented film extrusion |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 W-GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
- PEAK Werkstoff DISPAL S220 Aluminum Alloy, AlSi35, Condition O
- Plaskolite West Optix® CA - 75 LL General Purpose Acrylic Resin
- Kraton® D1119 P (SIS) Linear Block Copolymer
- Kingfa FRHIPS-930 Flame Retardant Polystyrene
- DuPont Teijin Films Teijin® Tetoron® U4 Polyester Film, 200 Gauge
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 25% Cold Reduction + Aged 538°C (1000°F)/4hr/AC
- BASF Petra® 130 FR 30% Glass Filled PET
- Amity Thermosets ATG 115 Phenolic Molding Organic Filler, Compression Molded
- 3M 8430-9 Cold Shrink Connector Insulators
Copyright © lookpolymers.com All Rights Reserved