DuPont Performance Polymers Crastin® 6130 NC010 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® 6130 NC010 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Crastin® 6130 NC010 is an unreinforced, medium high viscosity polybutylene terephthalate resin for extrusion and injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Water Absorption 0.070 %
<br>@Temperature 23.0 °C
 0.070 %
<br>@Temperature 73.4 °F
 22h @ 23°C(73°F); ASTM D570
Linear Mold Shrinkage 0.016 cm/cm
0.016 in/in
Flow
0.016 cm/cm
0.016 in/in
Transverse
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
Annealed; ISO 294-4
0.016 cm/cm
<br>@Thickness 2.00 mm
 0.016 in/in
<br>@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.021 cm/cm
0.021 in/in
Annealed; ISO 294-4
0.015 cm/cm
<br>@Thickness 2.00 mm
 0.015 in/in
<br>@Thickness 0.0787 in
 ISO 294-4
Melt Flow 15.4 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 15.4 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 ISO 1133
15.5 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 15.5 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength 12.0 MPa
<br>@Temperature 149 °C
 1740 psi
<br>@Temperature 300 °F
 ASTM D638
20.0 MPa
<br>@Temperature 90.0 °C
 2900 psi
<br>@Temperature 194 °F
 ASTM D638
55.0 MPa
<br>@Temperature 23.0 °C
 7980 psi
<br>@Temperature 73.4 °F
 ASTM D638
93.0 MPa
<br>@Temperature -40.0 °C
 13500 psi
<br>@Temperature -40.0 °F
 ASTM D638
Tensile Strength, Yield 59.0 MPa
<br>@Temperature 23.0 °C
 8560 psi
<br>@Temperature 73.4 °F
 ISO 527
Elongation at Break 11 %
<br>@Temperature -40.0 °C
 11 %
<br>@Temperature -40.0 °F
 ASTM D638
50 %
<br>@Temperature 23.0 °C
 50 %
<br>@Temperature 73.4 °F
 nominal; ISO 527
110 %
<br>@Temperature 23.0 °C
 110 %
<br>@Temperature 73.4 °F
 50mm/min; ISO 527
>= 300 %
<br>@Temperature 23.0 °C
 >= 300 %
<br>@Temperature 73.4 °F
 ASTM D638
>= 300 %
<br>@Temperature 90.0 °C
 >= 300 %
<br>@Temperature 194 °F
 ASTM D638
>= 300 %
<br>@Temperature 150 °C
 >= 300 %
<br>@Temperature 302 °F
 ASTM D638
Elongation at Yield 8.0 %
<br>@Temperature 23.0 °C
 8.0 %
<br>@Temperature 73.4 °F
 ISO 527
Tensile Modulus 2.60 GPa
<br>@Temperature 23.0 °C
 377 ksi
<br>@Temperature 73.4 °F
 ISO 527
Flexural Strength 8.00 MPa
<br>@Temperature 149 °C
 1160 psi
<br>@Temperature 300 °F
 ASTM D790
13.0 MPa
<br>@Temperature 90.0 °C
 1890 psi
<br>@Temperature 194 °F
 ASTM D790
80.0 MPa
<br>@Temperature 23.0 °C
 11600 psi
<br>@Temperature 73.4 °F
 ASTM D790
120 MPa
<br>@Temperature -40.0 °C
 17400 psi
<br>@Temperature -40.0 °F
 ASTM D790
Flexural Modulus 0.234 GPa
<br>@Temperature 149 °C
 33.9 ksi
<br>@Temperature 300 °F
 ASTM D790
0.331 GPa
<br>@Temperature 90.0 °C
 48.0 ksi
<br>@Temperature 194 °F
 ASTM D790
2.413 GPa
<br>@Temperature 23.0 °C
 350.0 ksi
<br>@Temperature 73.4 °F
 ASTM D790
3.00 GPa
<br>@Temperature -40.0 °C
 435 ksi
<br>@Temperature -40.0 °F
 ASTM D790
Compressive Strength 75.0 MPa
<br>@Temperature 23.0 °C
 10900 psi
<br>@Temperature 73.4 °F
 ASTM D695
Izod Impact, Notched 0.260 J/cm
<br>@Temperature -40.0 °C
 0.487 ft-lb/in
<br>@Temperature -40.0 °F
 ASTM D256
0.480 J/cm
<br>@Temperature 23.0 °C
 0.899 ft-lb/in
<br>@Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched NB
<br>@Temperature -40.0 °C
 NB
<br>@Temperature -40.0 °F
 ASTM D4812
NB
<br>@Temperature 23.0 °C
 NB
<br>@Temperature 73.4 °F
 ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
<br>@Temperature 23.0 °C
 1.90 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact, Notched 0.450 J/cm²
<br>@Temperature -30.0 °C
 2.14 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 179/1eA
0.500 J/cm²
<br>@Temperature 23.0 °C
 2.38 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C
<br>@Temperature -40.0 - 23.0 °C
 278 µin/in-°F
<br>@Temperature -40.0 - 73.4 °F
 ASTM E 831
500 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 278 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ASTM E 831
500 µm/m-°C
<br>@Temperature 55.0 - 160 °C
 278 µin/in-°F
<br>@Temperature 131 - 320 °F
 ASTM E 831
500 µm/m-°C
<br>@Temperature -40.0 - 23.0 °C
 278 µin/in-°F
<br>@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 278 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C
<br>@Temperature 55.0 - 160 °C
 278 µin/in-°F
<br>@Temperature 131 - 320 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
<br>@Temperature -40.0 - 23.0 °C
 50.0 µin/in-°F
<br>@Temperature -40.0 - 73.4 °F
 ASTM E 831
90.0 µm/m-°C
<br>@Temperature -40.0 - 23.0 °C
 50.0 µin/in-°F
<br>@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
144 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 80.0 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ASTM E 831
144 µm/m-°C
<br>@Temperature 23.0 - 55.0 °C
 80.0 µin/in-°F
<br>@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
162 µm/m-°C
<br>@Temperature 55.0 - 160 °C
 90.0 µin/in-°F
<br>@Temperature 131 - 320 °F
 ASTM E 831
162 µm/m-°C
<br>@Temperature 55.0 - 160 °C
 90.0 µin/in-°F
<br>@Temperature 131 - 320 °F
 ISO 11359-1/-2
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
225 °C
437 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
ISO 75-1/-2
150 °C
302 °F
ASTM D648
180 °C
356 °F
Annealed; ISO 75-1/-2
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
<br>@Temperature 23.0 °C
 1.00e+14 ohm-cm
<br>@Temperature 73.4 °F
 ASTM D257
>= 1.00e+15 ohm-cm
<br>@Temperature 23.0 °C
 >= 1.00e+15 ohm-cm
<br>@Temperature 73.4 °F
 IEC 60093
Surface Resistance 3.00e+12 ohm
<br>@Temperature 23.0 °C
 3.00e+12 ohm
<br>@Temperature 73.4 °F
 ASTM D257
Dielectric Constant 3.0
<br>@Frequency 1000 Hz,<br> Temperature 23.0 °C
 3.0
<br>@Frequency 1000 Hz,<br> Temperature 73.4 °F
 ASTM D150
3.0
<br>@Frequency 1.00e+6 Hz,<br> Temperature 23.0 °C
 3.0
<br>@Frequency 1.00e+6 Hz,<br> Temperature 73.4 °F
 ASTM D150
3.2
<br>@Frequency 1.00e+6 Hz,<br> Temperature 23.0 °C
 3.2
<br>@Frequency 1.00e+6 Hz,<br> Temperature 73.4 °F
 IEC 60250
Dielectric Strength 14.0 kV/mm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 356 kV/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 Short Time; ASTM D149
22.0 kV/mm
<br>@Thickness 1.60 mm,<br> Temperature 23.0 °C
 559 kV/in
<br>@Thickness 0.0630 in,<br> Temperature 73.4 °F
 Short Time; ASTM D149
Dissipation Factor 0.0020
<br>@Frequency 1000 Hz,<br> Temperature 23.0 °C
 0.0020
<br>@Frequency 1000 Hz,<br> Temperature 73.4 °F
 ASTM D150
0.020
<br>@Frequency 1.00e+6 Hz,<br> Temperature 23.0 °C
 0.020
<br>@Frequency 1.00e+6 Hz,<br> Temperature 73.4 °F
 ASTM D150
Comparative Tracking Index 600 V
<br>@Temperature 23.0 °C
 600 V
<br>@Temperature 73.4 °F
 UL 746A