- Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
- Chase Plastics CP Pryme® A110 ABS, 10% Glass Fiber Reinforced
Chase Plastics CP Pryme® A110 ABS, 10% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® A110 ABS, 10% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Glass fiber reinforcementInjection moldingForm: PelletsInformation provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Filler Content | 10 % | 10 % | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 241 PC
- Polymer Resources PC-FR2A-D Polycarbonate, Flame Retardant, Medium Flow
- Taiwan Sheen Soon Sheenthane® A8900F Thermoplastic Polyurethane Elastomer
- Solvay Technyl® A 205F Nylon 66, EH50
- ChevronTexaco TDH® Special Oil
- 3M FV513 Semi-Rigid Vinyl Label Product
- LATI Latilub 66-01M PA66, Molybdenum disulphide Filled
- 3M Dyneon™ CC605 Custom Fluoropolymer Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved