- A. Schulman ComAlloy Hiloy® 514 Polycarbonate, Glass Reinforced, UL
A. Schulman ComAlloy Hiloy® 514 Polycarbonate, Glass Reinforced, UL
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 514 Polycarbonate, Glass Reinforced, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 131 MPa | 19000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Izod Impact, Notched | 1.71 J/cm | 3.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ASTM D648 |
| Glass Transition Temp, Tg | 145 - 150 °C | 293 - 302 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 304 - 321 °C | 579 - 610 °F |
Users viewing this material also viewed the following:
- Pyrotek Pyroboard™ S1090 Roller
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR Sulfur
- LATI Latene® EP 22UVH2 MX/25 PP Copolymer, Mineral Reinforced
- Saint-Gobain COHRlastic® 3010 Low Temperature Flexibility Silicone Coated Fabric
- Silberline Tufflake® 3700
- Shinkong Synthetic Fibers Shinite® D202G15 PBT, 15% Glass Filled, Fire Retardant
- Polyram PlusTek RA846 Nylon 6.6, Impact Modified
- DSM Novamid® 2030 FC PA666
- DuPont Performance Polymers Delrin® 100TL NC010 Acetal (POM) (Unverified Data**)
- ExxonMobil Santoprene® 121-75M200 Thermoplastic Vulcanizate - UV Resistant
Copyright © lookpolymers.com All Rights Reserved