- Solvay TECHNYL® C 218 V33 PA6, 33% glass fiber, Eh 0
Solvay TECHNYL® C 218 V33 PA6, 33% glass fiber, Eh 0
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 218 V33 PA6, 33% glass fiber, Eh 0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA6, reinforced with 33% of glass fiber, heat stabilized, for injection molding.Applications: It has good mechanical properties, it is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. It is used in the automotive industry and electrical sectors.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Water Absorption | 0.92 % @Temperature 23.0 °C, Time 86400 sec |
0.92 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 193 MPa | 28000 psi | ISO 527 Type 1A |
| Elongation at Break | 3.1 % | 3.1 % | ISO 527 Type 1A |
| Tensile Modulus | 10.2 GPa | 1480 ksi | ISO 527 Type 1A |
| Flexural Modulus | 9.66 GPa | 1400 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1eA |
| Charpy Impact, Notched | 1.59 J/cm² | 7.57 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.8 | 3.8 | IEC 60250 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C |
Users viewing this material also viewed the following:
- Okulen® 2000 PE-UHMW, GB
- Quantum Composites QC-8850 43% Glass Fiber Reinforced Polyester Hybrid SMC
- PolyMirae Moplen HP640N Injection Molding Grade Polypropylene
- Overview of materials for Polyphenylene Sulfide (PPS); Molded
- Menzolit Menzolit® SMC 0412 Unsaturated Polyester UP
- Techmer ES Electrablend® PA6/6 C BK
- Loctite® 713 Accelerator for cyanoacrylates
- Braskem TI4130G Impact Copolymer Polypropylene
- Dow Corning 2-9034 EMULSION
- Resinlab® EP1285HD-14 Highly Filled, Medium Viscosity Casting Resin
Copyright © lookpolymers.com All Rights Reserved