Solvay TECHNYL® A 402 Natural FA PA66, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 402 Natural FA PA66, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced polyamide PA66, very high viscosity, for extrusion.Available in: Europe and North AmericaProduct Applications: TECHNYL® A 402 NATURAL FA offers three main advantages: high impact resistance at low humidity levels, good rigidity, and excellent compression resistance. This grade is particularly suitable for the molding of plastic insulators for railway binding and for extrusion of plates and profiles. Suitable for food contact applications (films, packaging, …). This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A |
| Water Absorption | 1.5 % @Temperature 23.0 °C, Time 86400 sec |
1.5 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 type 1 A |
| Elongation at Break | 60 % | 60 % | ISO 527 Type 1A |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527 type 1 A |
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO 527 Type 1A |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75/Af |
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 240 - 250 °C | 464 - 482 °F | |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.10 % | <= 0.10 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 240-260°C | |
| Draw-plate temperatures | 260-270°C |
Users viewing this material also viewed the following:
- PolyOne Geon™ HTX E1502 Polyvinyl Chloride Alloy (PVC Alloy)
- Imerys G-20 HP Feldspar
- Lucite International Elvacite ® 2614 Acrylic Resin
- SABIC Innovative Plastics LNP LUBRICOMP RFN18 PA 66 (Europe-Africa-Middle East)
- Goodfellow Nickel 80/Molybdenum 20 Alloy
- Plastics Group Polifil® GFPPCC-10 10% Glass Reinforced Polypropylene
- Chesterton ARC 982 100% Novolac acid resistant coating
- Fainplast Compounds GS 74/P Flexible PVC, Injection Molding for Footwear
- Ascend Performance Materials Vydyne® R543H Nylon 66, 43% Glass Filled, Dry as Molded
- Okulen® 500 PE-HMW, Natural
Copyright © lookpolymers.com All Rights Reserved