Solvay TECHNYL® A 230 V13 PA66, 13% glass fiber, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 230 V13 PA66, 13% glass fiber, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Modified polyamide 66, reinforced with 13% of glass fiber, with improved impact resistance, for injection molding.Available in: Europe and North AmericaProduct Applications: In addition to primary polyamide properties, TECHNYL® A230 V13 offers a very good rigidity / impact resistance compromise. This grade is used in the automotive industry, such as: belt covers, fasteners. This product is available in natural, black, grey, and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 type 1 A |
| Elongation at Break | 60 % | 60 % | ISO 527 Type 1A |
| Tensile Modulus | 3.65 GPa | 529 ksi | ISO 527 Type 1A |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60243 |
| Dissipation Factor | 0.050 | 0.050 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 265 °C | 500 - 509 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ NN-30GF/13T-2S Black Polyamide 66 (Nylon 66)
- SABIC Innovative Plastics Lexan® 133R PC (Asia Pacific)
- Polymer Resources PC-GP4 Polycarbonate, General Purpose, Easy Flow
- Arlon R3313X016-38 0.0165" (0.419 mm) Cured Silicone Rubber with Fiberglass Substrate 38" Wide (dis
- Lehmann & Voss LUVOCOM® 1301-8457 PPS, linear, with carbon fiber, lubricant modified
- Michelman® Michem® Emulsion 48625M1 Polymer solution
- A. Schulman PP 829-01 Polypropylene Homopolymer Polypropylene
- A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR Hi-Sil 233 Filler
Copyright © lookpolymers.com All Rights Reserved