Addiplast Addilene H 542 Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene H 542 Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced, high heat resistance, antistaticInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183/A |
| Melt Flow | 20 g/10 min | 20 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 74 | 74 | ISO 868 |
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO R 527 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ISO R 527 |
| Elongation at Yield | >= 100 % | >= 100 % | ISO R 527 |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | ISO 179/IeU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75-2/AF |
| Vicat Softening Point | 153 °C | 307 °F | ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | CEI 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | CEI 60093 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- LATI Latigloss 62 H2 G/50 PA 6, 50% Glass Fiber Reinforced, Heat Stabilized
- Sumitomo Chemical Sumipex® LG35 Acrylic Resin, High Flow
- ExxonMobil 763 Mobilmet 760 Series
- Tra-Con Tra-Bond F199 High Temperature Anaerobic Adhesive System
- Cadi 30WC Tungsten Copper
- DuPont™ Surlyn® 1707 Sodium Ionomer
- Vyncolit Neopreg Kinel® SK4504 S12 Carbon Reinforced Molding Compound
- PolyOne Therma-Tech™ ES-5500C TC-EM Polyethersulfone (discontinued **)
- LNP Lubricomp® QFL-4017 ER HS Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant (discontinu
Copyright © lookpolymers.com All Rights Reserved