Lanxess Pocan® TP 740-101 000000 PBT + ASA, 15% Glass Fiber
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® TP 740-101 000000 PBT + ASA, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT+ASA, 15% glass fibers, injection molding, low tendency to warp, improved surface finish
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.385 g/cc | 0.05004 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Melt Flow | 76 g/10 min @Load 5.00 kg, Temperature 270 °C |
76 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 - 250 °C | 437 - 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 °C | 518 °F | Injection Molding; ISO 294 |
| Mold Temperature | 90.0 °C | 194 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Form | Pellets | |
| ISO Shortname | ISO 7792-1-PBT+PET+ASA,GHMR,09-060,GF15 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Multibase TPSiV® 4200-80A Thermoplastic Elastomer
- Lehmann & Voss LUVOCOM® 50/CF/10/TF/15/BK 100 Polycarbonate, with carbon fiber and PTFE
- SABIC Innovative Plastics LNP LUBRICOMP JX91198 PES
- SABIC Innovative Plastics NORYL GTX APS440 PPE+PPS (Asia Pacific)
- EMS-Grivory Grivory® TSGL-50/4 black 9833 PA666-GF50
- Fainplast Compounds Hax™ HFC 0108 Flame Retardant Polyolefin Cable Compound
- 3M FV052R Tire Vinyl Label Products
- Aaron Industries AAROPRENE® GFPP 2010 Glass Filled Polypropylene
- Solvay Specialty Polymers Primef® 4002 40% GF PPS, High Fluidity Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved