Solvay TECHNYL® A 218C V10 PA66, 10% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218C V10 PA66, 10% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® A 218C V10 is a polyamide 66, reinforced with 10% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: Due to specially developed additives, the product offers a good electrical conductivity, combined with a good dimensional stability.Available in: Latin AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: It is mostly used for fuel or oil filters.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/A |
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec |
1.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 Type 1A |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 Type 1A |
| Tensile Modulus | 5.50 GPa | 798 ksi | ISO 527 Type 1A |
| Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C | 450 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 260-280°C | |
| Mixing Zone | 260-280°C |
Users viewing this material also viewed the following:
- MV Labs CO1000 CoSO4·6H2O Cobalt(II) sulfate hydrate
- PolyOne Dynaflex™ D3202-1000-03 Thermoplastic Elastomer (TPE)
- Polymax® Maxelast® C4900 TPE, Transparent
- Gouda Vuurvast CURON 145 CC Dense Refractory Castable
- Sylvin Technologies 9950-85 Natural PVC Molding Compound
- Eurotec® Tecomid® NA40 NL XA 20 PA 6.6 unreinforced, UL94 V0
- BASF HDO® 1,6-Hexanediol Flakes
- BASF Elastollan® 1180A10 Wire & Cable Grade Polyurethane Elastomer
- Overview of materials for Polypropylene with 30% Mica Filler
Copyright © lookpolymers.com All Rights Reserved