SABIC Innovative Plastics LNP THERMOCOMP RF004XXH PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF004XXH PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF004XXH is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added feature of this grade is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.440 % | 0.440 % | 23°C / 50% RH; ISO 62 |
| 0.780 % | 0.780 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 148 MPa | 21500 psi | 5 mm/min; ISO 527 |
| 149 MPa | 21600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| 2.8 % | 2.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.64 GPa | 1110 ksi | 1 mm/min; ISO 527 |
| 7.98 GPa | 1160 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 217 MPa | 31500 psi | ISO 178 |
| 233 MPa | 33800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 6.40 GPa | 928 ksi | 2 mm/min; ISO 178 |
| 7.13 GPa | 1030 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.93 J/cm | 11.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 241 °C | 466 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Network Polymers Kepital® F30-03
- Plastcom SLOVALEN PH 66 GF 30 FRO 4 PP, 30% glass fibre, mod. of mech. prop.
- Lord Adhesives Chemglaze® 9951 Standard Thinner
- Solvay TECHNYL® A 218 PA66, 33% glass fiber, Conditioned
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- A. Schulman POLYBATCH™ Light Grey LL803366/4 Concentrate Based In LLDPE
- ExxonMobil Santoprene® 203-50 Thermoplastic Elastomer
- 3M Hi-Strength 94 ET Spray Adhesive-Low VOC
- Addiplast Addinyl C2 ZV15 Nylon 66/6, 15% Glass Filled
- Tipco Tipcolene® FPDG-M FPDG M - 28% Talc/Mineral Reinforced Polypropylene Copolymer, High Stiffness & Impact Strength
Copyright © lookpolymers.com All Rights Reserved