- Solvay TECHNYL® A 218 S30 Black 21 N PA66, 30% glass fiber, DRY
Solvay TECHNYL® A 218 S30 Black 21 N PA66, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 S30 Black 21 N PA66, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA66, reinforced with 30% of glass spheres, heat stabilized, for injection molding.Available in: EuropeProduct Applications: TECHNYL® A 218 S30 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is recommended for mechanical components which require a very good surface finish with low warpage, and good compression strength. ( bearing housings ). This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Water Absorption | 0.75 % @Temperature 23.0 °C, Time 86400 sec |
0.75 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 type 1 A |
| Elongation at Break | 9.0 % | 9.0 % | ISO 527 Type 1A |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 Type 1A |
| Flexural Modulus | 3.85 GPa | 558 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² | 1.19 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Meilian Chemical W9350 WHITE MASTERBATCH
- Struktol V-HRW LUBRICANT ADDITIVE FOR PVC AND POLYMER PROCESSING
- Styrolution Polystyrol 454 C GR 2 PS
- A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene
- Covestro Bayfill® EA 6004 Polyurethane Energy-Absorbing Semi-Rigid Foam, Recoverable Grade, MDI-based 2-Component Liquid System
- Clariant PCSP0014 GREY Polycarbonate, Stainless Steel Fiber, EMI
- Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Conditioned (2.5% Moisture)
- Blue River Coatings Primer Sealer-PSWP
- Chesterton 860 Moldable Polymer Gasketing
Copyright © lookpolymers.com All Rights Reserved