- Solvay TECHNYL® A 218 MZ15 V 25 PA66, 25/15% glass/mineral fiber, DRY
Solvay TECHNYL® A 218 MZ15 V 25 PA66, 25/15% glass/mineral fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 MZ15 V 25 PA66, 25/15% glass/mineral fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® A 218 MZ15 V25 is a polyamide 66, reinforced with 25% of glass fiber and 15% of mineral filler, heat stabilized, for injection molding. This product is available in black color.Benefits: The product offers an excellent combination between thermal and mechanical properties as well as a low warpage of molded parts.Available in: Asia Pacific, Europe, Latin America and North America.Regulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applicationsApplications: This grade is commonly used in the automotive industry to mould large parts such as rocker cover and engine covers.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183/A |
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0066 cm/cm | 0.0066 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0101 cm/cm | 0.0101 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A |
| 150 MPa | 21800 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 Type 1A |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| 220 MPa | 31900 psi | ASTM D790 | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| 9.60 GPa | 1390 ksi | ASTM D790 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75/Af |
| 240 °C | 464 °F | ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C | |
| Draw-plate temperatures | 280-290°C |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO-LOCK SERIES 20 Anaerobic Thread Locking Compound
- Kennametal Stellite Deloro® 711 PM cast
- Mar-Bal MB3000-15NY Thermoset Polyester Composite Molding Compound
- Karina 1000/00856-IE MBPEB White
- Teknor Apex APEX® 3311-50 Polyvinyl Chloride, Flexible
- Samsung Cheil Industries Starex® TX-0520T TRABS, Unreinforced
- ChevronTexaco Miltex EP NLGI Grade 2
- Daikin POLYFLON MG-1241 PTFE 20% Glass Fiber and 5% Graphite Filled Molding Powder
- Fainplast Compounds FR 70/1 Flexible PVC, Insulation
Copyright © lookpolymers.com All Rights Reserved