Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
Manufacturer | Solvay |
Trade Name | Technyl® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Solvay TECHNYL® A 216 V30 Natural FA PA66, 30% glass fiber, DRY.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
Water Absorption | 0.80 % @Temperature 23.0 °C, Time 86400 sec |
0.80 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
Linear Mold Shrinkage | 0.0062 cm/cm | 0.0062 in/in | Isotropy |
Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |
Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 Type 1A |
Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 Type 1A |
Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/1A |
Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/1eU |
Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Melting Point | 263 °C | 505 °F | ISO 11357 |
Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/Af |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Constant | 3.75 | 3.75 | IEC 60250 |
Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243 |
Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
Comparative Tracking Index | 500 V | 500 V | Solution B; IEC 60112 |
600 V | 600 V | Solution A; IEC 60112 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
Drying Temperature | 80.0 °C | 176 °F | |
Moisture Content | <= 0.20 % | <= 0.20 % |
Descriptive Properties | Value | Comments |
---|---|---|
Compression Zone | 270-280°C |