Solvay TECHNYL® A 216 V20 PA66, 20% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 216 V20 PA66, 20% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 20% of glass fiber, for injection molding.Available in: Europe Product Applications: TECHNYL® A 216 V20 is used in all sectors of industry, offering and excellent combination between thermal and mechanical properties. This grade is used in: Automotive industry, Manufacture of components for electrical tools and Transport and building. This product is available in natural and black, and in a wide range of standard colors.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183/A |
| Water Absorption | 1.0 % @Temperature 23.0 °C, Time 86400 sec |
1.0 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0074 cm/cm | 0.0074 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0095 cm/cm | 0.0095 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | ISO 527 Type 1A |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 Type 1A |
| Tensile Modulus | 7.40 GPa | 1070 ksi | ISO 527 Type 1A |
| Flexural Modulus | 6.40 GPa | 928 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
Ignition Temperature; ISO 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+13 ohm | 6.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 525 V | 525 V | Solution B; IEC 60112 |
| 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Radici Radilon® S RV150 (dry) Nylon 6
- Karina E KAPU 6535/1-NT-MARFIM Ivory Compound (SP31502)
- Malvern Minerals Wollastokup® FF Silane Treated Wollastonite
- Kostat 5000 TAB Spacer Tapes PET
- LG Chemical M-Xylene
- LG Chemical LUPOL LW4405 PP+GF/MF40%
- Solvay RHODAFAC® ASI-100 Octyl phosphonic acid
- DuPont Teijin Films Mylar® D804 Polyester Film, 60 Gauge
Copyright © lookpolymers.com All Rights Reserved