| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Flame retardant polyamide 66, reinforced with 35% of glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America.Product Applications: This phosphorous flame retardant grade, UL 94 V0 (0.8 mm), offers excellent filling qualities and with good mechanical properties. This grade is suitable for molding insulating parts for electrical devices: connectors, switches, bobbins coil formers and thin parts under stress. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183/A |
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 190 MPa | 27600 psi | ISO 527 type 1 A |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 type 1 A |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527 Type 1A |
| Flexural Strength | 260 MPa | 37700 psi | ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
ISO 1210 |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
ISO 1210 | |
| Oxygen Index | 30.5 % | 30.5 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 325 V | 325 V | Solution B; IEC 60112 |
| 400 V | 400 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 275 - 280 °C | 527 - 536 °F | |
| Front Barrel Temperature | 290 - 295 °C | 554 - 563 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 285-290°C |
Users viewing this material also viewed the following:
- MV Labs LI300 Li2CO3 Lithium carbonate
- Premix Thermoplastics PRE-ELEC® TPE 1503 Conductive Thermoplastic Compound
- Polymax® Maxelast® D6770 TPE, Extruded
- Nilit Nilamid B3 H G10 50% Glass Fiber Reinforced PA6
- Polymer Resources NY66-IM1-[color]-H Nylon 66, Medium Impact Modified, Heat Stabilized
- M Chemical GUARD DOGâ„¢ UV328 Benzotriazole UV Absorber
- Techmer ES HiFill FR® TPX-PBT-01006 40% Glass/Ceramic Filled
- Teknor Apex APEX® 90-A41R-65-NT Polyvinyl Chloride, Flexible
- A. Schulman PP 3486-01 Polypropylene Homopolymer Polypropylene
- Unitika RUN35-C25 PA6, Dry
Copyright © lookpolymers.com All Rights Reserved