- Polyphenylene Sulfide (PPS), Unreinforced, Extruded
- Solvay Specialty Polymers Ryton® QC160P Polyphenylene Sulfide (PPS)
Solvay Specialty Polymers Ryton® QC160P Polyphenylene Sulfide (PPS)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Unreinforced, Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Ryton® QC160P Polyphenylene Sulfide (PPS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ryton® QC160P (pelletized) polyphenylene sulfide exhibits excellent thermal stability and chemical resistance and is suitable for thermoplastic extrusion processes.Features: Good Chemical Resistance; Good Thermal StabilityAdditional Properties: Ash Content - ISO 3451-1 0.3 wt%; Volatiles - (150°C): < 0.3 wt%Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
ISO 62 |
| Melt Flow | 45 g/10 min @Load 5.00 kg, Temperature 316 °C |
45 g/10 min @Load 11.0 lb, Temperature 601 °F |
Procedure B; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 75.0 MPa | 10900 psi | ISO 527-2 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527-2 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527-2 |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ISO 178 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm |
0.993 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | Notch A; ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
27.8 µin/in-°F @Temperature -58.0 - 122 °F |
2 |
| 120 µm/m-°C @Temperature 100 - 200 °C |
66.7 µin/in-°F @Temperature 212 - 392 °F |
2 | |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 280 °C | 536 °F | ISO 11357-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | >= 180 °C | >= 356 °F | ISO 306 |
| Glass Transition Temp, Tg | 90.0 °C | 194 °F | ISO 11357-2 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 44 % | 44 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Natural | |
| Form | Pellets | |
| Processing Technique | Extrusion | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE EC90 D50 P05B Thermoplastic Elastomer, PP/EPDM
- H.C. Starck Amperit® 538.074 Agglomerated, Sintered Tungsten Carbide-Tungsten Boride-Cobalt (WC-WB-Co ) 60-30-10
- LG Chemical XR404HJ ABS, Heat Resistance, Curl Fit
- Stratasys® Ultem 9085 for Rapid Prototyping