Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride (discontinued **)

Category	Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In addition to standard molding and extrusion, Hylar® polymers lend themselves well to solution-applied coatings.

Physical Properties	Metric	English	Comments
Density	1.77 - 1.79 g/cc	0.0639 - 0.0647 lb/in³	ASTM D792
Water Absorption	0.020 %	0.020 %	ASTM D570
Linear Mold Shrinkage	0.025 - 0.030 cm/cm	0.025 - 0.030 in/in
Melt Flow	8.0 - 10 g/10 min @Load 3.80 kg	8.0 - 10 g/10 min @Load 8.38 lb

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	76 - 80	76 - 80	ASTM D2240
Tensile Strength, Ultimate	35.0 - 45.0 MPa	5080 - 6530 psi	ASTM D638
Tensile Strength, Yield	34.0 - 48.0 MPa	4930 - 6960 psi	ASTM D638
Elongation at Break	50 - 250 %	50 - 250 %	ASTM D638
Elongation at Yield	10 %	10 %	ASTM D638
Tensile Modulus	1.70 - 3.10 GPa	247 - 450 ksi	ASTM D638
Flexural Yield Strength	55.0 - 76.0 MPa	7980 - 11000 psi	ASTM D790
Flexural Modulus	1.73 - 2.41 GPa	251 - 350 ksi	ASTM D790
Izod Impact, Notched	0.800 - 1.30 J/cm	1.50 - 2.44 ft-lb/in
Izod Impact, Unnotched	>= 15.0 J/cm	>= 28.1 ft-lb/in	Low Temp; ASTM D256
Coefficient of Friction, Dynamic	0.12 - 0.15	0.12 - 0.15	ASTM D1894
Coefficient of Friction, Static	0.10 - 0.15	0.10 - 0.15	ASTM D1894

Thermal Properties	Metric	English	Comments
CTE, linear	100 - 120 µm/m-°C @Temperature 20.0 °C	55.6 - 66.7 µin/in-°F @Temperature 68.0 °F	ASTM D696
Specific Heat Capacity	1.50 J/g-°C	0.359 BTU/lb-°F	DSC
Thermal Conductivity	0.190 - 0.220 W/m-K	1.32 - 1.53 BTU-in/hr-ft²-°F	ASTM C177
Melting Point	165 - 168 °C	329 - 334 °F	ASTM D3418
Maximum Service Temperature, Air	150 °C	302 °F	No oxidative or thermal degradation after 5 years at 150°C (300°F)
Deflection Temperature at 1.8 MPa (264 psi)	105 - 115 °C	221 - 239 °F	TMA
Brittleness Temperature	<= -30.0 °C	<= -22.0 °F	ASTM D2236
Flammability, UL94	V-0	V-0
Oxygen Index	44 %	44 %	ASTM D2863

Optical Properties	Metric	English	Comments
Refractive Index	1.42	1.42

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.25e+15 ohm-cm	1.25e+15 ohm-cm	ASTM D257
Dielectric Constant	5.6 @Frequency 1e+6 Hz	5.6 @Frequency 1e+6 Hz	ASTM D150
	6.9 @Frequency 60 Hz	6.9 @Frequency 60 Hz	ASTM D150
Dielectric Strength	13.0 kV/mm @Thickness 3.20 mm	330 kV/in @Thickness 0.126 in	Short-Time 500 V/sec
Dissipation Factor	0.035 @Frequency 60 Hz	0.035 @Frequency 60 Hz	ASTM D150
	0.158 @Frequency 1e+6 Hz	0.158 @Frequency 1e+6 Hz	ASTM D150
Arc Resistance	>= 50 sec	>= 50 sec	ASTM D495

Processing Properties	Metric	English	Comments
Processing Temperature	215 - 232 °C	419 - 450 °F	Preheat