Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Typical applications include electrical and electronic components especially for automotive systems. - Black: AS-4133 HS BK 324 - Natural: AS-4133 HS NTInjection Notes: Injection Rate: 3 to 4 in/sec Holding Pressure: 50% of injection pressureData is presented for dry polymer.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.45 g/cc	0.0524 lb/in³	ISO 1183/A
Filler Content	33 %	33 %	Glass Fiber Reinforcement
Water Absorption	0.29 % @Time 86400 sec	0.29 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 cm/cm	0.0050 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	79.3 MPa @Temperature 175 °C	11500 psi @Temperature 347 °F	ISO 527-2
	87.6 MPa @Temperature 150 °C	12700 psi @Temperature 302 °F	ISO 527-2
	125 MPa @Temperature 100 °C	18100 psi @Temperature 212 °F	ISO 527-2
	211 MPa @Temperature 23.0 °C	30600 psi @Temperature 73.4 °F	ISO 527-2
Tensile Strength	200 MPa	29000 psi	ASTM D638
Elongation at Break	2.5 %	2.5 %	ASTM D638
	2.6 % @Temperature 23.0 °C	2.6 % @Temperature 73.4 °F	ISO 527-2
	4.3 % @Temperature 100 °C	4.3 % @Temperature 212 °F	ISO 527-2
	6.6 % @Temperature 150 °C	6.6 % @Temperature 302 °F	ISO 527-2
	6.6 % @Temperature 175 °C	6.6 % @Temperature 347 °F	ISO 527-2
Tensile Modulus	11.7 GPa	1700 ksi	ASTM D638
	4.83 GPa @Temperature 175 °C	701 ksi @Temperature 347 °F	ISO 527-2
	5.31 GPa @Temperature 150 °C	770 ksi @Temperature 302 °F	ISO 527-2
	6.83 GPa @Temperature 100 °C	991 ksi @Temperature 212 °F	ISO 527-2
	12.6 GPa @Temperature 23.0 °C	1830 ksi @Temperature 73.4 °F	ISO 527-2
Flexural Strength	290 MPa	42100 psi	ASTM D790
	99.3 MPa @Temperature 175 °C	14400 psi @Temperature 347 °F	ISO 178
	111 MPa @Temperature 150 °C	16100 psi @Temperature 302 °F	ISO 178
	177 MPa @Temperature 100 °C	25700 psi @Temperature 212 °F	ISO 178
	296 MPa @Temperature 23.0 °C	42900 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
	4.21 GPa @Temperature 175 °C	611 ksi @Temperature 347 °F	ISO 178
	4.62 GPa @Temperature 150 °C	670 ksi @Temperature 302 °F	ISO 178
	7.17 GPa @Temperature 100 °C	1040 ksi @Temperature 212 °F	ISO 178
	10.4 GPa @Temperature 23.0 °C	1510 ksi @Temperature 73.4 °F	ISO 178
Compressive Strength	179 MPa	26000 psi	ASTM D695
Poissons Ratio	0.41	0.41	ASTM E132
Shear Modulus	4.15 - 4.47 GPa	602 - 648 ksi	Calculated
Shear Strength	89.6 MPa	13000 psi	ASTM D732
Izod Impact, Notched	0.800 J/cm	1.50 ft-lb/in	ASTM D256
	9.60 J/cm	18.0 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	9.70 kJ/m²	4.62 ft-lb/in²	ISO 180/1A
Izod Impact, Unnotched (ISO)	59.0 kJ/m² @Temperature 23.0 °C	28.1 ft-lb/in² @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	6.70 J/cm²	31.9 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	1.10 J/cm²	5.23 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	15.0 µm/m-°C @Temperature 100 - 200 °C	8.33 µin/in-°F @Temperature 212 - 392 °F	TMA; ASTM E831
	20.0 µm/m-°C @Temperature 0.000 - 100 °C	11.1 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	76.0 µm/m-°C @Temperature 0.000 - 100 °C	42.2 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E831
	120 µm/m-°C @Temperature 100 - 200 °C	66.7 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
Melting Point	327 °C	621 °F	ISO 11357-3
	327 °C	621 °F	ASTM D570
Maximum Service Temperature, Air	210 °C @Time 5.40e+6 sec	410 °F @Time 1500 hour	Continuous; ASTM D3045
Deflection Temperature at 0.46 MPa (66 psi)	320 °C @Thickness 3.20 mm	608 °F @Thickness 0.126 in	Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	294 °C	561 °F	Unannealed; ISO 75-2/A
	300 °C @Thickness 3.20 mm	572 °F @Thickness 0.126 in	Annealed; ASTM D648
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+16 ohm-cm	2.00e+16 ohm-cm	ASTM D257
Dielectric Constant	3.6 @Frequency 1.00e+6 Hz	3.6 @Frequency 1.00e+6 Hz	ASTM D150
	3.8 @Frequency 60.0 Hz	3.8 @Frequency 60.0 Hz	ASTM D150
Dielectric Strength	20.0 kV/mm @Thickness 1.60 mm	508 kV/in @Thickness 0.0630 in	ASTM D149
Dissipation Factor	0.0040 @Frequency 60.0 Hz	0.0040 @Frequency 60.0 Hz	ASTM D150
	0.012 @Frequency 1.00e+6 Hz	0.012 @Frequency 1.00e+6 Hz	ASTM D150
Comparative Tracking Index	600 V	600 V	UL 746
High Voltage Arc-Tracking Rate, HVTR	14.0 mm/min	0.551 in/min	UL 746

Processing Properties	Metric	English
Rear Barrel Temperature	318 - 324 °C	604 - 615 °F
Front Barrel Temperature	327 - 332 °C	621 - 630 °F
Melt Temperature	329 - 343 °C	624 - 649 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.045 %	0.045 %

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer
	Lubricant
	Mold Release
Appearance	Black
	Natural Color
Automotive Specifications	ASTM D4000 PA102 G35 Color: BK324 Black
	ASTM D4000 PA102 G35 Color: NT Natural
	ASTM D4000 PPA0121 G34 GB145 KD170 KN100 PN060 YI285 Color: BK324 Black
	ASTM D4000 PPA0121 G34 GB145 KD170 KN100 PN060 YI285 Color: NT Natural
	ASTM D6779 PA102G35
	BOSCH N28 BN05-OX2 BN0515-GF35-3Anf01AM Color: NT Natural
	BOSCH N28 BN05-OX2 BN0515-GF35-3Asw01AM Color: BK324 Black