- Eurotec® Tecolen® CP20 GB30 NL PPCP, 30% glass bead reinforced, natural
Eurotec® Tecolen® CP20 GB30 NL PPCP, 30% glass bead reinforced, natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Glass Bead Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecolen® CP20 GB30 NL PPCP, 30% glass bead reinforced, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527 |
| Tensile Modulus | 1.50 GPa | 218 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 - 165 °C | 320 - 329 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 - 240 °C | 392 - 464 °F | |
| Feed Temperature | <= 60.0 °C | <= 140 °F | Throat |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Chevron Phillips Marlex® HXM 50100-02 Extra high molecular weight hexene copolymer (discontinued **)
- LATI Laticonther 83 CP/85 PA12, Impact Modified
- Techmer ES HiFill® PA6/6 GF20 L BK 20% Glass Filled
- SABIC Innovative Plastics Valox® IQ420HP PBT
- Polyplastics Duranex® CN5330 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 30% GF filled
- A. Schulman POLYBATCH™ Treated Pine 60175U/4 Concentrate Based In LLDPE
- ExxonMobil 100 Mobil DTE PM Series
- Fainplast Compounds Hax™ CAT 111 Catalyst for Cable Compound
- Arkema Group Rilsan® BECN W3 TL Nylon 11, Sheathing Grade (Dry)
Copyright © lookpolymers.com All Rights Reserved