SABIC Innovative Plastics LNP THERMOCOMP 9H1100C
| Category | Polymer , Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 9H1100C.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* 9H1100C is a High Specific Gravity compound containing proprietary fillers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 11.29 g/cc | 11.29 g/cc | ASTM D792 |
| Density | 11.26 g/cc | 0.4068 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 12.0 MPa | 1740 psi | Type I, 5 mm/min; ASTM D638 |
| 13.0 MPa | 1890 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | Type I, 5 mm/min; ASTM D638 |
| 13.0 MPa | 1890 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 0.80 % | 0.80 % | 5 mm/min; ISO 527 |
| 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.96 GPa | 429 ksi | 1 mm/min; ISO 527 |
| 5.49 GPa | 796 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 25.0 MPa | 3630 psi | ISO 178 |
| Flexural Yield Strength | 25.0 MPa | 3630 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.09 GPa | 738 ksi | 2 mm/min; ISO 178 |
| 6.57 GPa | 953 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.78 J/cm | 3.33 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Reliance Industries METABOLIX PHO
- Magyar Aluminum ALOLT 730 Aluminum Hydroxide
- GRECO ISOTHANE 2058A Poly(caprolactone)ester TPUÂ Resin
- SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66
- A. Schulman POLYBATCH™ Grey 8899 Concentrate Based In Polyethylene
- A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene
- Westlake EM808AA Low Density Polyethylene
- Hippe SI GC 41 Woven Glass Cloth Reinforced Silicone Resin - Round, Molded Tube and Rod
- Clariant Renol ABS3470 ABS, High Heat, Low Gloss
- DuPont Performance Polymers VTR 8525 (GBLT-S) Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinued
Copyright © lookpolymers.com All Rights Reserved