BASF Ultraform® H2320 004 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer BASF
Trade Name Ultraform®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform® H2320 004 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Is a POM, high-molecular-weight grade for extrusion of small thin-walled pipes and panel.Information provided by BASF
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C; 50% RH; ISO 62
Melt Flow 3.08 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 3.08 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 130 MPa

@Load 36.5 kg,
Time 30.0 sec
 18900 psi

@Load 80.5 lb,
Time 0.00833 hour
 ISO 2039-1
Tensile Strength, Yield 64.0 MPa
9280 psi
50 mm/min; ISO 527-2
Elongation at Break 32 %
32 %
50mm/min; ISO 527-2
Elongation at Yield 11 %
11 %
ISO 527-2
Modulus of Elasticity 2.60 GPa
377 ksi
ISO 527-2
Izod Impact, Notched (ISO) 6.50 kJ/m²
3.09 ft-lb/in²
ISO 180/A
Charpy Impact Unnotched 21.0 J/cm²

@Temperature -30.0 °C
 99.9 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
25.0 J/cm²

@Temperature 23.0 °C
 119 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²

@Temperature -30.0 °C
 2.62 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1000 hours 1300 MPa
189000 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C

@Temperature 23.0 - 55.0 °C
 66.7 µin/in-°F

@Temperature 73.4 - 131 °F
 DIN 53752
Melting Point 166 °C
331 °F
DIN 53765
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
ISO 75-2
Vicat Softening Point 150 °C
302 °F
ISO 306
Decomposition Temperature >= 240 °C
>= 464 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 IEC 60250
3.8

@Frequency 100 Hz
 3.8

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 40.0 kV/mm
1020 kV/in
IEC 60243-1
Dissipation Factor 0.0010

@Frequency 100 Hz
 0.0010

@Frequency 100 Hz
 IEC 60250
0.0050

@Frequency 1.00e+6 Hz
 0.0050

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Test solution A; IEC 60112
600 V
600 V
Test solution B; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 190 - 230 °C
374 - 446 °F
Injection-molding
Mold Temperature 60.0 - 120 °C
140 - 248 °F
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature 320-340 °C
ASTM D1929
Primary Processing Technique Extrusion and Injection Molding