- Thermoplastic
- ABS Polymer
- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Sax Polymers SAXLAC 420HI Acrylonitrile Butadiene Styrene
Sax Polymers SAXLAC 420HI Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Sax Polymers |
| Trade Name | SAXLAC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXLAC 420HI Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Saxalac 420HI is a flame retardant, very high flow ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 7.0 g/10 min @Load 5.00 kg, Temperature 220 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| 60 g/10 min @Load 10.0 kg, Temperature 220 °C |
60 g/10 min @Load 22.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 40.0 MPa | 5800 psi | ISO 527-1 |
| Elongation at Break | 15 % | 15 % | ISO 527-1 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 4.20 J/cm² @Temperature -30.0 °C |
20.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 80.0 °C @Thickness 2.00 mm |
176 °F @Thickness 0.0787 in |
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 93.0 °C | 199 °F | 50B; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
|
| Glow Wire Test | 750 °C | 1380 °F | IE/CEN 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 HS-GV50 Nylon 6.6 for injection molding, 50% glass fiber reinforced
- DuPont Performance Polymers Delrin® 527UV BK701 Acetal Homopolymer (Unverified Data**)
- Lehmann & Voss LUVOCOM® 1105-8127-1 PEEK, lubricant modified
- Solvay Specialty Polymers Ryton® BR42B Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Solvay ANTAROX® L 62N Surfactant
- A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene
- Elastron® D SEBS Elastomer
- 3M FM058 Indoor UL Recognized Brite Silver Polyester Label Products
- ExxonMobil Mobil 1 75W-90 Gear Lubricant LS
Copyright © lookpolymers.com All Rights Reserved