- Sax Polymers SAXATEC 4307 Acrylonitrile Styrene Acrylate
Sax Polymers SAXATEC 4307 Acrylonitrile Styrene Acrylate
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Sax Polymers |
| Trade Name | SAXATEC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXATEC 4307 Acrylonitrile Styrene Acrylate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXATEC 4307 is a high impact resistant, high viscosity and weatherable ASA injection molding grade, characterized by high mechanical strength and good processabilityInformation provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 45.0 MPa | 6530 psi | ISO 527-1 |
| Elongation at Break | 15 % | 15 % | ISO 527-1 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 180 |
| 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact Unnotched | 5.20 J/cm² @Temperature -30.0 °C |
24.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.30 J/cm² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 95.0 °C @Thickness 2.00 mm |
203 °F @Thickness 0.0787 in |
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 93.0 °C | 199 °F | 50B; ISO 306 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE144H PC (Asia Pacific)
- Technetics Group Amicon™ Nylon 6/66 (Unverified Data**)
- SABIC Innovative Plastics NORYL WCA871 PPE-TPE (Asia Pacific)
- Sharadaa Ceramics LI SILL-I High Alumina Brick
- American Elements Manganese Oxide Nanopowder
- Loctite® 3532 High viscosity Dam Encapsulant
- DSM Fibre Intermediates Nyrim® 2025 (Wollastocoat®), Dry
- CMW® ELKONITE® 3150 Silver Tungsten Carbide contact material ASTM B663 Table 2, Class B
- 3M Scotchcal™ ElectroCut™ 7125-10 Graphic Film
- Plansee MLR Molybdenum-Lanthanum Oxide; Recrystallized
Copyright © lookpolymers.com All Rights Reserved