BASF Novolen® 1040 K Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 1040 K Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Melt Flow | 4.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | |
| Elongation at Break | 20 % | 20 % | |
| Elongation at Yield | 7.0 % | 7.0 % | |
| Tensile Modulus | 1.90 GPa | 276 ksi | |
| Charpy Impact Unnotched | 13.0 J/cm² | 61.9 ft-lb/in² | |
| 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | |
| 0.150 J/cm² @Temperature -30.0 °C |
0.714 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 135 µm/m-°C @Temperature 20.0 °C |
75.0 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |
| Vicat Softening Point | 102 °C | 216 °F | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.000070 @Frequency 100 Hz |
0.000070 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled
- SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS
- Teknor Apex Monprene® MP-2242 Thermoplastic Elastomer
- Wieland 1916 Wilaform Gold
- CP-Polymer-Technik Wellamid® 6000 MR 309 HWCP Mineral Nylon 6, Heat Stabilized, Conditioned
- ChevronTexaco Superla® 21 White Oil
- Akzo Nobel Trigonox® F-C30 Polymerization Initiator
- BASF Novolen® 2448 L Polypropylene
- Asahi Kasei Xyron® 300H Modified Polyphenylene Ether
- ChevronTexaco Havoline® MERCON®/DEXRON®-III Automatic Transmission Fluid
Copyright © lookpolymers.com All Rights Reserved