Teknor Apex APEX® 6500-105 Polyvinyl Chloride, Flexible
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Flexible Grade , PVC, Wire and Cable Grade |
| Manufacturer | Teknor Apex Company |
| Trade Name | APEX® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex APEX® 6500-105 Polyvinyl Chloride, Flexible.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: 60°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Extrusion Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molded Components Additional Information: Temperature Rating: 60°CInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore C | 80 | 80 | 10 seconds; ASTM D2240 |
| Tensile Strength at Break | 20.7 MPa | 3000 psi | ASTM D638 |
| Elongation at Break | 280 % | 280 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -10.0 °C | 14.0 °F | ASTM D746 |
| UL RTI, Electrical | 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746 |
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746 |
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V @Thickness 3.00 mm |
>= 600 V @Thickness 0.118 in |
UL 746 |
| Hot Wire Ignition, HWI | >= 120 sec @Thickness 3.00 mm |
>= 120 sec @Thickness 0.118 in |
UL 746 |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 3.00 mm |
>= 120 arcs @Thickness 0.118 in |
UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 °C | 380 °F | Processing Temperature |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent |
Users viewing this material also viewed the following:
- Plaskolite Duraplex® 100% I Impact Modified Acrylic Sheet
- SABIC Innovative Plastics Lexan® HPS1R PC (Asia Pacific)
- Lehmann & Voss LUVOCOM® 1-7139 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized
- Momentive Performance Materials RTV116 Red Adhesive Sealant, High Temperature Pourable
- Solvay Specialty Polymers Tecnoflon® FOR 3390 Fluoroelastomer
- Styron XZ 94462.01 Carboxylated SB
- Teijin Panlite® LV-2225Z Transparent and Weather Resistant grade Polycarbonate Resin
- A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene
- BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Dry)
- ACC QSil 58 QSI Quantum Silicones 50 Durometer Condensation Cure for Potting
Copyright © lookpolymers.com All Rights Reserved