Samyang Trirex® 3025G15 Polycarbonate, 15% Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® 3025G15 Polycarbonate, 15% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries.Characteristics:Medium viscosity10% glass fiberApplications:3025R type reinforced by glass fiber (short fiber). particularly suitable for injection molding where especially good dimensional stability is requiredAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Water Absorption | 0.12 % @Time 86400 sec |
0.12 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm @Thickness 3.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 93.2 MPa | 13500 psi | ASTM D638 |
| Elongation at Break | 11 % | 11 % | ASTM D638 |
| Flexural Yield Strength | 147 MPa | 21300 psi | ASTM D790 |
| Flexural Modulus | 4.41 GPa | 640 ksi | ASTM D790 |
| Izod Impact, Unnotched | 1.57 J/cm @Thickness 3.17 mm |
2.94 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 33.0 µm/m-°C | 18.3 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 151 °C | 304 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.05 @Frequency 1.00e+6 Hz |
3.05 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | ASTM D149 |
| Dissipation Factor | 0.0097 @Frequency 1.00e+6 Hz |
0.0097 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Middle Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Front Barrel Temperature | 280 - 300 °C | 536 - 572 °F | |
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |
| Melt Temperature | 300 - 310 °C | 572 - 590 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Screw Speed | 30 - 80 rpm | 30 - 80 rpm |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable MJF114A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Huntsman Araldite GT 6063 Bisphenol A Epoxy Solid Resin
- Iran Petrochemical (PCC) 2102TX00 Low Density Polyethylene
- Samsung Cheil Industries Infino® QP-1010 PC/ABS, Unreinforced FR
- A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade
- A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene
- Covestro Makrolon® 1804 Polycarbonate
- 3M Scotchcal™ 50-54 Graphic Film
- API Megol AM DP1741 SEBS Adhesion Modified Overmolding for PA
- A. Schulman POLYFORT™ FPP 3727 Mineral Filled Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved