Aclo Accutech Polypropylene Homopolymer HP0339C40L Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339C40L Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ASTM D638 |
| Flexural Strength | 37.0 MPa | 5370 psi | ASTM D790 |
| Flexural Modulus | 2.699 GPa | 391.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.352 J/cm | 0.660 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F |
Users viewing this material also viewed the following:
- Mytex Polymers AS66K-01 Polypropylene, Talc filled, Compounded
- Pacific Sintered Materials FN-255-S(HT) Nickel Steel Powdered Metal
- SABIC Innovative Plastics Ultem 1000FV PEI
- Taiwan Sheen Soon Sheenthane® AH-592 TPU for Hotmelt Adhesive
- SGL Carbon Group PANOX® SM C076 SSC Oxidized Textile Fiber, Crimped staple fiber, For felts and non-wovens
- DSM Akulon® K223-TP4 (Dry) Impact Modified Nylon 6 (North America)
- A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer
Copyright © lookpolymers.com All Rights Reserved