Samyang Triel® 5400 Thermoplastic Polyether Ester Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5400 Thermoplastic Polyether Ester Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRIEL® resins offer superior mechanical properties, elasticities, heat and chemical resistance, which allow it to be widely used for electric/electronic equipments, automotive parts and outdoor recreation equipments. TRIEL® can be processed by a variety of thermoplastic processing techniques like injection molding, extrusion and extrusion blow molding.Grade Characteristics:Chemical resistanceApplications:Belt, SealAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 0.45 % @Time 86400 sec |
0.45 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.014 - 0.015 cm/cm | 0.014 - 0.015 in/in | ASTM D955 |
| Melt Flow | 15 - 18 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 - 18 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 40 | 40 | ASTM D2240 |
| Tensile Strength, Yield | 2.16 - 2.35 MPa @Strain 5.00 % |
313 - 341 psi @Strain 5.00 % |
ASTM D638 |
| 4.22 - 4.41 MPa @Strain 10.0 % |
612 - 640 psi @Strain 10.0 % |
ASTM D638 | |
| 7.65 - 7.85 MPa @Strain 50.0 % |
1110 - 1140 psi @Strain 50.0 % |
ASTM D638 | |
| Elongation at Break | >= 400 % | >= 400 % | ASTM D638 |
| Flexural Yield Strength | 3.92 MPa | 569 psi | ASTM D638 |
| Flexural Modulus | 0.0226 GPa | 3.27 ksi | ASTM D790 |
| Izod Impact, Unnotched | NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256 |
| NB @Temperature -23.0 °C |
NB @Temperature -9.40 °F |
ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 32 | 32 | CS-17 Wheel; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 200 °C | 392 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | Rate B; ASTM D648 |
| Vicat Softening Point | 143 °C @Load 1.02 kg |
289 °F @Load 2.25 lb |
Rate B; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 170 - 220 °C | 338 - 428 °F | Injection or Extrusion |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Injection |
| 190 - 230 °C | 374 - 446 °F | Extrusion | |
| Front Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Injection |
| 190 - 220 °C | 374 - 428 °F | Extrusion | |
| Nozzle Temperature | 180 - 220 °C | 356 - 428 °F | Injection |
| Die Temperature | 190 - 220 °C | 374 - 428 °F | Extrusion |
| Drying Temperature | <= 100 °C | <= 212 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | <= 0.030 % | <= 0.030 % | |
| Injection Pressure | 5.90 - 7.90 MPa | 856 - 1150 psi | |
| Cycle Time - Injection | 1.2 - 1.5 sec | 1.2 - 1.5 sec | |
| Cycle Time - Cooling | 10 - 20 sec | 10 - 20 sec |
Users viewing this material also viewed the following:
- Outokumpu 4435 Cr-Ni-Mo Austenitic Stainless Steel
- Solvay Chemicals Ammonium Fluoride Grade 2 Aqueous solution of ammonium fluoride 40%
- SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+PS
- Zotefoams Evazote® EV50 Ethylene Vinyl Acetate Copolymer Foam
- A. Schulman SCHULAMID® 6 NV12 Easy Flow Low Viscosity Nylon 6
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR Sulfur
- Dow Corning 2-8839 EMULSION
- Aremco Ceramabind™ 830 High Temperature Inorganic Binder
- Braskem CP 286 Injection Molding Polypropylene Heterophasic Copolymer
Copyright © lookpolymers.com All Rights Reserved